SYNTHESIS AND CHARACTERIZATION OF LIQUID CRYSTALLINE COPOLYESTERS WITH X-SHAPED TWO-DIMENSIONAL MESOGENIC UNITS AND CROWNETHER CYCLE OF Cis-4,4′-bis(4-hydroxy PHENYLAZO) DIBENZO- 14- CROWN-4
SJ Zheng,XH Xu,JW Wang,SY Zhang,Y Du,XW Li,ZF Li,QF Zhou
DOI: https://doi.org/10.3724/sp.j.1105.2006.00236
2006-01-01
Abstract:A novel series of main chain liquid crystalline copolyesters with X-shaped two-dimensional mesogenic units and crown ether cycles of cis-4,4'-bis(4-hydroxyphenylazo) dibenzo-14-crown-4 was synthesizeed via solution cocondensation polymerizations from 4, 4'-(alpha, omega-octanedioylxy)dibenzoyl dichloride (M-1), 2, 5-bis (p-dodecyloxybenzoyloxy) hydro-quinone (M-2) and cis-4,4'-bis(4-hydroxyphenylazo)dibenzo-14-crown-4 (M-3) as the monomers. Monomer M, was synthesized by esterification and substitution reaction of p-hydroxybenzoic acid and octanedioyl chloride. Monomer M, was synthesized by esterfication and reduction reaction of 2, 5-dihydroxybenzoquinone and p-dodecyloxybenzoyl chloride. Monomer (M-3) was synthesized by diazotization and coupling reaction of cis-diaminodibenzo-14-crown-4 and phenol. The molecular weights of copolyesters are not high, and the [eta] of the copolyesters ranges from 0.35 similar to 0.25 dL/g. The monomer structures were identified by using elementary analysis, IR, UV, H-1-NMR and MS etc. All the copolyester samples are yellowish powders and insoluble at room temperature in THF and CHCl3 except for sample CP9. The properities of copolyesters were investigated by using GPC, [eta], DSC, TG, WAXD and POM. It was found that all the copolyesters went into liquid-crystal phase when they were heated over their melting temperature (T-m). The thread texture and schlieren texture can be observed. Their melting temperature and isotropic temperature (T-1) change regularly with varying the cis-4,4'-bis(4-hydroxyphenylazo)dibenzo-14-crown-4 unit content in the copolyesters. The WAXD study illustrated that the copolyesters are liquid crystalline with a nematic phase. A dispersive peak at 2 theta near 20 degrees appeared in their WAXD patterns, which is a typical character for quenched nematic liquid crystal copolyesters.