Effects of RE on Microstructures and Properties of Al-20Si-2Cu-1Ni Aluminum Alloy

Zhong Gu,Wu Zhibin,Wu Shusen,Nagaumi Hiromi

2016-01-01

Rare Metal Materials and Engineering

Abstract:The effects of Ce-rich Rare Earth (RE) on modification of eutectic silicon, formation of RE compound, and mechanical properties of Al-20Si-2Cu-1Ni high silicon aluminum alloy have been studied by optical microscope (OM), scanning electron microscopy (SEM), and energy dispersive spectrometry (EDS). The mechanism was also discussed. The results show that, RE can modify eutectic silicon effectively which show better modification with increasing amounts of RE. While it also causes the formation of needle-like RE compounds, which increase in quantity with more RE. The mechanism of eutectic silicon modification is that the growth of eutectic silicon is hindered by the RE elements enriched at solidification front. But the excess RE will lead to the formation of acicular Al2Si2RE compound containing a few solutions of Cu and Ni elements which can offset partially the improvement of mechanical properties contributed by eutectic silicon modification. As a result, the mechanical performances of this alloy decrease with more acicular Al2Si2RE compounds. With addition of 0.6% RE to the melt, the tensile strength and elongation of cast high silicon aluminum alloy reach maximum values which are improved by 33% and 230%, respectively, compared to the case without RE.