Effects of Si and RE on the microstructure and properties of AZ31 magnesium alloy

李继强,贾志欣,刘文,刘立君
DOI: https://doi.org/10.3969/j.issn.1001-9731.2012.20.031
2012-01-01
Abstract:The effects of Si-RE on the microstructure and mechanical properties of AZ31magnesium alloy were investigated. The phase present in the alloys have been identified by optical metallography(OM), scanning elec- tron microscopy(SEM) /energy dispersive X-ray spectroscopy(EDS) and X-ray diffractometer (XRD). And the mechanical properties have also been measured by material test machine at room temperature. The results show that he microstructure is obviously refined and the tensile strength of AZ31 based alloy at room temperature is significantly improved. Compared to AZ31, the tensile of AZ31 0.4%Si 0.5%RE alloy has higher ultimate ten sile strength and elongation. Its ultimate tensile strength and elongation are enhanced by 42MPa and 3.9%, re- spectively. Although addition alloy elements can't change the fracture mode of AZ31, SEM fractographs of ten- sile fracture surface have obvious plastic deformation. It indicates that has had the bigger plastic deformation before failure.
What problem does this paper attempt to address?