Abstract:Fe-10%Ni alloys were synthesized in a high energy horizontal rotary ball mill from pure element Fe and Ni powders. Phase constitution, shape and thermal stability of the milled powders were characterized using X-ray diffractometry (XRD), scanning electron microscopy (SEM) and differential thermal analysis (DTA), respectively. And microstructure and properties of bulks prepared by hot-press sintering with milled powders as starting materials were analyzed and tested. Results indicate that under the condition of a milling speed of 400 r/min and a ball-to-powder mass ratio of 20:1, Ni fully solubilizes in Fe, which forms a supersaturate solid solution of Fe(Ni) with a body-centered cubic structure. Particles of the powder milled up to 16 h are more homogeneous and finer than those of the powder milled for 8 h, but phase of the powder is still Fe(Ni) solid solution. The alloy powder milled for 16 h were annealed in the temperature range between 500 and 800 degrees C. It is found that structure of the powder after annealing is stable and no phase transformation occurs in the powder. Phase of the powder is still Fe(Ni) solid solution. When the alloy powders milled for 16 h were treated by hot pressed sintering at 950 degrees C, a little Fe(Ni) solid solution with a face-centered cubic structure is found in the bulks. If the bulks that previously were treated by hot-press sintering at 950 degrees C and cooled to room temperature were subsequently sintered at 970 degrees C again, the phase of the powders completely transforms to Fe(Ni) solid solution with a face-centered cubic structure. However, the strength and ductility of bulks treated by hot-press sintering at 950 degrees C are superior to those of bulks by subsequent sintering at 970 degrees C, because oxide and holes are produced in resintered bulks without pressure.

Sintering Properties and Microstructure of Fe-Ni-Co-based Superalloy Atomized Powder

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

Research on Fe-10%Ni Alloy Synthesized by Mechanical Alloying

A novel method for preparing intermetallics/ superalloy dissimilar materials using current sintering of metallic powders

Microstructure and mechanical properties of liquid–phase sintered W@NiFe composite powders

Microstructure, Phase Transformation and Mechanical Property of Ni-Co-Mn-In Alloy Prepared by Spark Plasma Sintering

Influence of Co Content on the Microstructures and Mechanical Properties of a Ni–Co Base Superalloy Made by Specific Additive Manufacturing Process

Study on the process and microstructure of Fe34Mn13.5Al3Cr7.5Ni alloy prepared by spark plasma sintering based on elemental powder

Precipitation and Phase Transformation Mechanism of Additive Manufactured Ni-Co Base Superalloy

Effect of γ' phase and microtwins on the microstructural evolution and mechanical properties of a novel Ni–Co base superalloy

Correlation between microstructure and mechanical properties of novel Co-Ni-based powder metallurgy superalloy

Improvement In Microstructure Homogeneity Of Sintered Compacts Through Powder Treatments And Alloy Designs

Microstructure evolution, phase decomposition and transition of Al0.8Co0.5Cr1.5CuFeNi HEA during high temperature sintering and mechanical properties corresponding to different microstructures

Investigation of Phase Composition and Microstructure of the FeAl/Al<sub>2</sub>O<sub>3</sub> Composites Fabricated by Mechanical Alloying and Hot-Pressing Process

Effect of Melt Superheat Treatment on Solidification Behavior and Microstructure of New Ni–Co Based Superalloy

Microstructure and High-Temperature Mechanical Properties of CrMnFeCoNi/TiAl Composites Prepared by Powder Metallurgy

Effects of Fe on Microstructures and High-Temperature Compressive Mechanical Properties of Nb-16Si-22Ti-2Cr-2Al-2Hf Based Alloy

Research on the structure and mechanical properties of Ni-Cr-Co-W-Mo-Al-Ti porous superalloy

Preparation of Fe Coating Al<sub>2</sub>O<sub>3</sub> Nanometer Composite Powder and its Mechanical Properties after Hot Press Sintering

Improved Homogenization of Ni in Sintered Steels Through the Use of Cr-Containing Prealloyed Powders

Sintering mechanism and microstructure evolution of a CoCrFeNiMn high entropy alloy fabricated by metal injection molding