Abstract:The fracture behaviour of compact tension (CT) specimens of nickel-based single crystal superalloys DD3 has been studied at 760 degrees C, 850 degrees C and 950 degrees C and three different crack crystallographic orientations of (001)[100], (011)[100] and (111)[0-111. The macro crack growth paths, the fracture toughness and the micro fracture morphologies have been examined by optical microscope (OM) and scan electron microscope (SEM). A crystallographic plastic finite element method (FEM) has also been used to analyze the resolved shear stress distribution ahead of the cracks. The experimental and FEM results show that the crystallographic orientations have much influence on the crack growth path, the fracture toughness of specimen, and the stress characterization ahead of the cracks. At low temperature, e.g. 760 degrees C or 850 degrees C, the macroscopic crack growth path appears on the zigzag wave, but all the fracture surfaces are flat along the crack direction at high temperature, e.g., 950 degrees C. FEM analysis shows that the deformation and fracture ahead of the crack take place in the specific slip planes for different crack orientations. For the three specimens tested at 760 degrees C, the deflected angles of crack initiation direction with respect to crack plane are 45 degrees, 53.7 degrees and 90 degrees in the order of crack orientations of (001)[100], (0 11)[100] and (I 11)[0-111, respectively. The growth path of crack is agreement with the theoretical analyses by FEM. Furthermore, the temperature is another factor affecting the fracture of specimens. It is clear that the fracture mode of the CT specimens transfers from brittle to ductile with the temperature increasing.

Influence of Electron Beam Thermal Effect on Cracks Formation in Fused Region of Single Crystal Superalloys DD407

The Influence of Grain Boundary Angle on the Hot Cracking of Single Crystal Superalloy DD6

Effect of texture evolution and defect on the crack initiation of a Ni‐based superalloy electron beam welded joint

Analysis on the Microfissuring Behavior in the Heat-affected Zone of Electron-beam Welded Nickel-based Superalloy

Analysis of Cracks in the Electron Beam Welded Joint of K465 Nickel-Base Superalloy

In-situ Observation of Crack Initiation and Propagation in Ni-based Superalloy with Film Cooling Holes During Tensile Test

Crack propagation paths and fracture of Ni-based single crystal

Microstructure, mechanical properties and cracking behaviour in a γ′-precipitation strengthened nickel-base superalloy fabricated by electron beam melting

Study on Microfissuring Damage of Ni-base Superalloy under Thermal Shock of Electron-beam Welding

Stray grain formation, thermomechanical stress and solidification cracking in single crystal nickel base superalloy welds

Cracking behavior of Ti-48Al-2Cr-2Nb alloy in powder bed fusion electron beam melting process

Hot cracking behavior and mechanism of a third-generation Ni-based single-crystal superalloy during directed energy deposition

Formation Mechanisms of Hot Cracks in Laser Additive Repairing Single Crystal Superalloys

Investigation on the hot crack sensitivity of a nickel-based single crystal superalloy fabricated by epitaxial laser metal forming

Avoiding Cracks in Additively Manufactured Non-Weldable Directionally Solidified Ni-based Superalloys

Liquation Cracking Facilitated by Stray-Grain Chains in a High-Γ’-content Nickel-Based Alloy K4002 Produced Via Electron Beam Powder Bed Fusion

Analysis of liquation and solidification cracks in the electron beam welding of GTD-111 nickel-base superalloy joint

Crack generation mechanism and control method of electron beam welded Nb/GH3128 joint

Investigation of cracks during electron beam welding of γ-TiAl based alloy

Effect of crack on morphology evolution of the precipitates in Nickel-based superalloys under applied stress

Effects of Thermal Stress on the Formation and Cracking Behavior of Nickel-Based Superalloys by Selective Laser Melting Based on a Coupled Thermo-Mechanical Model