Abstract:The relevant phase transformations induced by atomic diffusion at the vicinity of Nb/TiAl heterogenous interface were systematically investigated by establishing a novel system of TiAl-Nb couple via metallurgical bonding of Nb block and γ-TiAl powders by hot pressing sintering and post-annealing treatments. As a result, the resultant diffusion layer, acting as adhesive region linking the Nb and TiAl substrates, thickened with the increase of annealing temperature and the prolongation of holding time, which could be well described by the developed power function. A series of intermediate phases initially nucleated at the Nb/TiAl interface and grew toward both substrates, which was the result of the exchange, partitioning and recombination of solute atoms in the light of vacancy-mediated substitutional diffusion pattern. The phase transformation path on the Nb side was β→η→η + σ→σ→β 0 →β 0 + γ n , while that on the TiAl side was γ→γ ss →γ ss + α→(γ + α)+ (α + β 0 )→α + β 0 →β 0 + γ n . Then the disorder-order transition of α→α 2 and β 0 →B2 occurred during cooling. The progress of phase transformation slowed down as the diffusion proceeded, which was attributed to the decrease in atomic substitution efficiency due to the reduction of atomic concentration gradient and the extension of migration distance. In such a case, the banded σ ba split into spike σ sp along the direction of maximum concentration gradient, and then shrunk to isolated σ is until completely dissolved in β 0 regime, principally dominated by Ti occupying Nb sublattices. The lenticular γ n existed mainly in the form of twins, resulting from the lattice reconstruction in accordance with the orientation relationship of 111γ//110β0 and 1̅10γ//11̅1β0 in the Al partitioning region during the spontaneous fluctuation of atomic concentration of β 0 regime. These findings filled some fundamental gaps with respect to TiAl-Nb diffusion reaction system, and afforded profound insights into the development of high-performance TiAl/Nb composites with tailorable microstructure.

NbTi superconductors with variable compositions produced by diffusion reaction of niobium and titanium sheets

EFFECTS OF DIFFERENT Ti CONTENT ON NbTi SUPERCONDUCTOR′S CRITICAL CURRENT DENSITIES

Fabrication of Nbti Superconducting Joint by Electromagnetic Forming Method

The Reaction Process of NbAl Interface in Rod-in-Tube Strands

Study on the Microstructure of High Magnetic Field (≥ 9 T) NbTi Superconducting Wire

Study on the property and microstructure of NbTiTa superconducting wire

Superconducting property improvement of RHQT Nb3Al wires through doping of Ti

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

Development of Electromagnetic Forming Nbti Superconducting Joint

Growth and superconductivity of niobium titanium alloy thin films on strontium titanate (001) single-crystal substrates for superconducting joints

Structure and Low-Temperature Interdiffusion of NbTi Superlattices

Penetration depth and critical fields in superconducting NbTi thin films grown by co-sputtering at room temperature

Microstructure Evolution and Diffusion Mechanism of Nb/TiAl Alloy Diffusion-Bonded Joints

Superconducting Connections Between NbTi Thin Films With NbN Paste

Fabrication of Low AC Loss Cu0.5Mn-Based NbTi Superconducting Strands

Atomic diffusion and microstructural evolution at the Nb/TiAl heterogenous interfaces during annealing at elevated temperatures

Preparation and Superconducting Properties of Thin Films of Some Binary Transition Metal Alloy Systems

Preparation and Properties of NbTi–Nb 3 Sn–NbTi Superconducting Joints

High-temperature magnetization and bulk magnetostriction investigation of Ti and Nb addition to Fe70Co30 alloy

Microstructure Evolution of As-Cast Nb-Ti-C Alloys

Niobium based intermetallics as a source of high-current/high-magnetic field superconductors