Abstract:Solution-processed transparent conductive oxides offer the advantages of low-cost, high-throughput fabrication of electronic devices compared to the specific requirements of vacuum deposition techniques. However, adapting the current state of the art to ink deposition calls for optimization of the precursor ink composition and the postdeposition process. Solution processing of indium tin oxide films can be accomplished at reduced temperatures (250-400 °C) by annealing soluble precursor metal salts together with a fuel/oxidizer, causing an exothermic reaction with elevated local temperatures. Following layer-by-layer cycles of deposition and annealing, a postprocessing step is required via heating (300 °C) under a 5% H2 reducing atmosphere. To address the discrepancy between the versatility of ink deposition and the limitations of controlled atmosphere postprocessing, here we investigate the effects of postprocess dipping in aqueous sodium borohydride at room temperature as an alternative, which allows for a completely solution-based process from ink to film. In addition to postprocessing, the solution composition was also optimized by removing the fuel additive and by adjusting the In/Sn content. Indium tin oxide (ITO) films were spin-coated and annealed in air at 250, 300, and 400 °C and characterized by UV/vis spectroscopy to obtain optical transmittance, atomic force microscopy to obtain film thickness and surface morphology, and a Hall effect system for electrical parameters. Additional data from X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) indicate that crystallinity is affected by the reducing environment. Results revealed an order-of-magnitude improvement of the Haacke figure of merit (FOM) from 4.3 × 10-4 Ω-1, 382 Ω/□ sheet resistance (Rs), and 84% transmittance (%T) for the traditional 9:1 In/Sn precursor ink with fuel additive followed by 300 °C of 5% H2-furnace post-treatment compared to that of the optimized fully solution-processed 8.5:1.5 In/Sn ink without fuel followed by an ambient air at 25 °C dipping in aqueous sodium borohydride, leading to 3.0 × 10-3 Ω-1 FOM, 84.5 Ω/□ Rs, and 87%T including the glass substrate.

Optimized Design for Preparing Nanocrystalline ITO Powder

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Gas Phase Fabrication of Morphology-Controlled ITO Nanoparticles and Their Assembled Conductive Films.

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

The Characterization And Preparation Of Nano-Scale Fe Doping Tio2 By Sol-Gel Method - (Ii) - The Crystal Character And Grain Growth Of Fe Doping Tio2 Xerogel Powders

Optimization Preparation of Indium Tin Oxide Nanoparticles via Microemulsion Method Using Orthogonal Experiment

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

pH control on preparation of nano-TiO_2 by gel-sol process

A Size-Controllable Preparation Method for Indium Tin Oxide Particles Using A Membrane Dispersion Micromixer

PREPARATION OF IRON-DOPED TITANIA NANOCRYSTALLINE GRAINS AND ITS PHOTOCATALYTIC PROPERTY

Synthesis of Tin Oxide Nanoparticles by Precipitation Process: Effects of pH and Temperature on the Particle Size and Morphology

Improvement of Electrochromic Performance by Embedding ITO Nanocrystals in Amorphous WO3 Film

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

A Study on the Influencing Factors in the Preparation of Bismuth-doped Tin Oxide Nano-powders by Co-Precipitation

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

OPTIMIZATION OF HEAT TREATMENT TECHNOLOGY OF NANO Al2O3 POWDERS

Preparation and characterization of hollow spherical indium tin oxide with micro size by template assisted hydrothermal method

Hydrothermal Preparation and Characterization of Nanocrystalline Porous Tin Dioxide Thin Films

Rheological properties of ITO slurries prepared from nano-powders for gelcasting process

The key of ITO films with high transparency and conductivity: Grain size and surface chemical composition

Room-Temperature Postannealing Reduction via Aqueous Sodium Borohydride and Composition Optimization of Fully Solution-Processed Indium Tin Oxide Films