Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Microstructural Evolution and Mechanical Behavior of Mg-10Y-2.45Zn-1Ca-0.37Al Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructure and Mechanical Properties of Mg–4.0Zn–0.5Ca Alloy

Microstructures and Mechanical Properties of Mg-2Y-xZn (x=1, 2, 3 At%) Alloys

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

Enhanced Performance of Mg–Zn–Y–Mn Alloy Via Minor Ca Addition

Microstructure and mechanical properties of as-cast ultralight and high strength Mg-10Li-3Al-3Zn-xY alloy with multi-precipitates

Effects of Al and Zn Contents on the Microstructure and Mechanical Properties of Mg-Al-Zn-Ca Magnesium Alloys

Effect of Al on Microstructure and Mechanical Properties of Mg-10Li-3Zn-1Y Alloys

Microstructure Evolution and Mechanical Properties of Mg-LPSO Two Phase Mg96Y2Ni2 (at. %) Alloy Processed by Hot Extrusion and Decreasing-Temperature ECAP

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Microstructure and mechanical properties synergistically enhanced via heat treatment modification of the as-extruded Mg-1.5Al-0.5Zn-0.2Y-0.2Ca alloy

Microstructure and Mechanical Properties of As-Cast and Solid Solution Treated Mg−8Li−xAl−yZn Alloys

Microstructure and Plastic Instability of Mg-4.3Li-1.08Y-5.83Zn Alloy

Effects of solid solution heat treatment on microstructures and mechanical properties of Mg96.82Gd2Zn1Zr0.18alloy with 14H-type LPSO structure

Microstructural Evolution and Mechanical Properties of Mg-5y-5gd-Xnd-0.5zr Magnesium Alloys at Different States

Microstructure And Mechanical Properties Of Mg-8li-4al-0.3y Alloys

Structural Features and Mechanical Properties of Mg-Y-Zn-Sn Alloys with Varied LPSO Phases

Microstructures and Mechanical Properties of Mg–10Gd–6Y–2Zn–0.6Zr(wt.%) Alloy

Microstructures and properties of as-cast rare Earth magnesium alloy with LPSO phase

Effects of an LPSO Phase Induced by Zn Addition on the High-Temperature Properties of Mg-9Gd-2Nd-(1.5Zn)-0.5Zr Alloy