Precipitation Kinetics and Coarsening Behavior of Multimodal gamma ' Microstructure in High Performance Ni-Base PM Superalloy

Zhang Ming,Liu Guoquan,Wang Hao,Huang Hailiang,Hu Benfu

2019-01-01

Rare Metal Materials and Engineering

Abstract:Differential scanning calorimetry (DSC) and thermal simulation continuous cooling experiments were used to study the behavior and microstructure of gamma' multi-generations precipitation during the continuous cooling process in the third generation high performance PM superalloy. The linear regression method was used to get the quantitative relationship between the average sizes of secondary gamma' and cooling rates, and the formation kinetics and mechanism of multimodal size distribution of gamma' precipitates on the gamma matrix were analyzed and discussed. The results show that the alloy can obtain a multimodal size distribution of gamma' precipitates at cooling rates less than 1.4 degrees C/s(-1). The multi-generations precipitation is closely related to the cooling rates. The slow cooling is the dominant reason for the multimodal size distribution of gamma' precipitates. Results of long-term aging of the alloy with gamma' multimodal size distribution show that reverse coarsening phenomenon occurs due to the unstable morphology of the large-size secondary gamma', i.e., the average size of gamma' precipitates decreases with the increase of aging time. This reverse coarsening effect increases the strength of the alloy, and increases the long-term stability of the microstructure of the alloy. The conditions and reasons for the reverse coarsening of gamma' were also discussed. This work will provide a theoretical basis for the further research and development of new high performance PM superalloys.