Characteristic of Hole Wall Trepanning by Picosecond Laser in Superalloy

Sun Ruifeng,Zhang Xiaobing,Cao Wenbin,Gong Shuili,Zhang Xiaopeng

2013-01-01

Rare Metal Materials and Engineering

Abstract:Picosecond laser trepanning drilling of the directional solidification Ni3Al-based superalloy of different thickness has been studied. The experiment demonstrates that there are periodic stripes in the hole wall, of which the interval is about 15 mu m. The stripes is the path formed by the laser ablation. It is showed that when the film-hole is drilled in 1mm thick alloy, the hole wall almost has no taper and no recast layer exists, while the thickness of alloy is 2 mm, the hole wall near the entrance appears a recast layer, of which thickness ranges from 2 mu m to 5 mu m. By comparison, the recast layer is mainly caused by the plasma deposited in the hole wall when the laser pulse width is 2.1 ps, and the reason of recast layer containing oxygen is that plasma and the oxygen of compressed air react chemically and deposits on the hole wall. In the surface of entrance of different thickness alloy, there is molten area of 5 mu m wide around the entrance of hole. Considering that the thermal diffusion can be ignored when the laser pulse width is 2.1 ps, the molten area can be explained according to the corresponding relationship between the temperature distribution of irradiated area and energy distribution of cross section of laser beam, and the width of molten area of entrance was calculated, it is in line with the actual width.