Abstract:Zeolites with different structures (P1, sodalite, and X) were synthesized from coal fly ash by applying ultrasonically assisted hydrothermal and fusion–hydrothermal synthesis. Bimetallic catalysts, containing 5 wt.% Ni and 2.5 wt.% Cu, supported on the zeolites, were prepared by a post-synthesis incipient wetness impregnation method. The catalysts were characterized by X-ray powder diffraction (XRPD), N2 physisorption, transmission electron microscopy (TEM), Mössbauer and X-ray photoelectron spectroscopies (XPS), and H2–temperature-programmed reduction (H2-TPR) analyses. The XRPD results showed that crystalline Cu0 and NixCuy intermetallic nanoparticles were formed in the reduced catalysts. The presence of the intermetallic phase affected the reducibility of the nickel by shifting it to a lower temperature, as confirmed by the H2-TPR curves. Based on the Mössbauer spectroscopic results, it was established that the iron contamination of the coal fly ash zeolites (CFAZs) was distributed in ionic positions of the zeolite lattice and as a finely dispersed iron oxide phase on the external surface of the supports. The formation of the NiFe alloy, not detectable by XRPD, was also evidenced on the impregnated samples. The catalysts were studied in the upgrading of levulinic acid (LA), derived from lignocellulosic biomass, to γ-valerolactone (GVL), in a batch reactor under 30 bar H2 pressure at 150 and 200 °C, applying water as a solvent. The NiCu/SOD and NiCu/X catalysts showed total LA conversion and a high GVL yield (>75%) at a reaction temperature of 200 °C. It was found that the textural parameters of the catalysts have less influence on the catalytic activity, but rather the stable dispersion of metals during the reaction. The characterization of the spent catalyst found the rearrangement of the support structure. The high LA conversion and GVL yield can be attributed to the weak acidic character of the support and the moderate hydrogenation activity of the Ni-Cu sites with high dispersion.

A practical and concise homogeneous nickel catalyst for efficient solvent-free synthesis of -valerolactone

Highly efficient Ni-Mn/SiO<sub>2</sub> catalyst for the selective hydrogenation of biomass-derived levulinic acid to -valerolactone under mild conditions

Hydrogenation of Levulinic Acid over Nickel Catalysts Supported on Aluminum Oxide to Prepare Γ-Valerolactone

Catalytic Hydrogenation of Levulinic Acid to Gamma-Valerolactone over Ni/ZrO2

Highly Efficient Selective Hydrogenation of Levulinic Acid to Γ-Valerolactone over Cu–Re/TiO2 Bimetallic Catalysts

An Efficient and Reusable Embedded Ru Catalyst for the Hydrogenolysis of Levulinic Acid to Γ‐valerolactone

Selective Production of gamma-Valerolactone and Valeric Acid in One-Pot Bifunctional Metal Catalysts

Synthesis of Γ-Valerolactone from Ethyl Levulinate Hydrogenation and Ethyl 4-Hydroxypentanoate Lactonization over Supported Cu-Ni Bimetallic, Bifunctional Catalysts

Selective Production of γ-Valerolactone from Biomass-Derived Levulinic acid over Ni/CMK-3 catalyst

Selective Conversion of Levulinic Acid to Gamma-Valerolactone over Ni-based Catalysts: Impacts of Catalyst Formulation on Sintering of Nickel

An Efficient and Reusable Bimetallic Ni3Fe NPs@C Catalyst for Selective Hydrogenation of Biomass-Derived Levulinic Acid to Γ-Valerolactone

A Nitrogen-Doped Carbon Modified Nickel Catalyst for the Hydrogenation of Levulinic Acid under Mild Conditions

The Formation of γ-Valerolactone from Renewable Levulinic Acid over Ni-Cu Fly Ash Zeolite Catalysts

Ion-Exchange Synthesis of Surrounded CoNi@Al2O3 Catalyst for Levulinic Acid Hydrogenation to γ-Valerolactone under Mild Conditions

Production of γ-Valerolactone from Methyl Levulinate via Catalytic Transfer Hydrogenation on Nickel-Copper Oxide Catalyst

Conversion of levulinic acid and formic acid into γ-valerolactone over heterogeneous catalysts.

Highly efficient CuNi-ZrO2 nanocomposites for selective hydrogenation of levulinic acid to γ-valerolactone

Bimetallic ordered mesoporous carbon from lignin for catalytic selective hydrogenation of levulinic acid to γ-valerolactone

Effect of method of preparation of Ni and/or Cu supported on ZSM-5 catalysts for the aqueous phase hydrogenation of levulinic acid to γ-valerolactone

Hierarchically porous single catalyst Ru/HPW/UiO-66 with synergistic acid/metal sites for one-pot catalytic synthesis of γ–Valerolactone

Levulinic acid hydrogenation to γ-valerolactone over single Ru atoms on a TiO 2 @nitrogen doped carbon support