Abstract:Humidity change in concrete is the leading cause of concrete shrinkage. Moreover, the moisture diffusion coefficient of concrete is an essential parameter for assessing and predicting the internal moisture content of concrete. However, there is a lack of theoretical construction and experimental studies on the effect of different conditions, especially different constraints, on the moisture diffusion coefficient of concrete. Therefore, the internal humidity, pore structure parameters, and basic mechanical properties of concrete under different strength grades C30, C40, C50, and C60 (C stands for concrete and numbers indicate the strength class of the concrete), curing environments (dry and sealed curing conditions), and constraints were tested in this study. In addition, a calculation model of concrete's internal humidity and humidity diffusion coefficient was established. The research findings show that the internal humidity of concrete decreased with age due to hydration and drying. External humidity had a significant effect on the moisture change of concrete, and the lower the external humidity, the larger the humidity diffusion coefficient and the faster the internal humidity of concrete decreases. Reinforcement (confinement) changes the pore structure parameters of the concrete, which in turn affects the transport of moisture within the concrete. The higher the reinforcement rate, the larger the pore structure parameters of the concrete, the larger the humidity diffusion coefficient, and the faster the concrete humidity decreases. The method proposed in the study can accurately predict the internal humidity of concrete using the humidity diffusion coefficient. The research results are a reference for preventing concrete shrinkage and cracking in construction.

INVESTIGATION ON THE INTERIOR RELATIVE HUMIDITY OF CONCRETE AT EARLY AGE

Development of Internal Humidity in Concrete at Early Ages

Interior Relative Humidity of Normal- and High-Strength Concrete at Early Age

Experimental Study on the Internal Relative Humidity in Concrete under Dry-Wet Cycles

Determination of Moisture Diffusion Coefficient of Concrete at Early Age from Interior Humidity Measurements

A Coupled Hygro-Thermal Model of Early-Age Concrete Based on Micro-Pore Structure Evolution

Integrative Studies on Autogenous and Drying Shrinkages of Concrete at Early-Age

Investigation on the Internal Relative Humidity of Superabsorbent Polymer–Modified Concrete Exposed to Various Ambient Humidities at Early Age

Moisture Movement in Early-Age Concrete under Cement Hydration and Environmental Drying

Moisture Diffusion Coefficient of Concrete under Different Conditions

Development of Shrinkage and Internal Moisture in Cement Paste,Mortar and Concrete at Early Age

Calculation of Moisture Distribution in Early-Age Concrete

Internal relative humidity and drying stress gradients in concrete

Influence of Pre-soaked Light-Weight Aggregate on Early-Age Interior Humidity Distribution and Development in Concrete Slab

Coupling Effect of Temperature and Relative Humidity Diffusion in Concrete under Ambient Conditions

Analysis on early-age inner stress in concrete structure

Experimental and Theoretical Studies on Autogenous Shrinkage of Concrete at Early Ages

Early Age Properties and Cracking Control of Concrete

Tests and Simulations of Interior Humidity and Shrinkage of Concrete under Sealed Condition

Interior Humidity of Concrete under Dry-Wet Cycles

Tests and Simulations on Shrinkage of Concrete at Early-Age