Abstract:Ordered large-pore (up to 12 nm) and stable mesoporous aluminophosphates (AlPO) have been synthesized by using block copolymer (EO106PO70EO106, Pluronic F127) as a structure-directing agent. The selection of inorganic precursors is based on an “acid–base pair” route. Three acid–base pair, including AlCl3/H3PO4, AlCl3/OP(OCH3)3 and Al(OC4H9)3/PCl3 are confirmed to be efficient for the assembly of periodic mesoporous frameworks. Ordered 2-D hexagonal mesoporous aluminophosphates can be obtained by using AlCl3/H3PO4 as precursors, while disordered mesoporous aluminophosphates are produced by using AlCl3/OP(OCH3)3 or Al(OC4H9)3/PCl3 as precursors. BET surface areas and pore sizes of the products vary from 261 to 115 m2/g and from 9.4 to 12 nm, respectively. The solution and solid state 27Al and 31P MAS NMR were used to characterize the chemical environment of aluminium and phosphorus before and after the formation of mesostructured AlPO products, which simultaneously allows us to evaluate the efficiency of inorganic–inorganic (I–I) interactions (Al–O–P) of different acid–base pair. Both 27Al and 31P MAS NMR results show that among the three acid–base pair, AlCl3/H3PO4 pair interacts more readily with each other than the other two pairs [AlCl3/OP(OCH3)3, Al(OC4H9)3/PCl3], and tends to form rigid framework before calcination. The detailed structural characterizations reveal that strong I–I interactions (Al–O–P) between inorganic precursors will lead to a final mesoporous material with high structure regularity. This method can also be applied to synthesize iron-incorporated aluminophosphate (FeAlPO) with highly ordered 2-D hexagonal structure. BET surface area and pore size of FeAlPO prepared with Fe/Al=0.1 (molar ratio) are 181 m2/g and 8.9 nm, respectively. Electron spin resonance (ESR) and UV–vis spectra were employed to characterize the chemical state of Fe3+ ion.

Synthesis of Mesoporous Titanium Phosphate with High Surface Area Using Long-Chain Alkylamine

Synthesis and Characterization of Mesoporous TiO2 with Wormhole-Like Framework Structure

Layer-by-layer Grafting of Titanium Phosphate Onto Mesoporous Silica SBA-15 Surfaces: Synthesis, Characterization, and Applications.

Synthesis and Characterization of Phosphated Mesoporous Titanium Dioxide with High Photocatalytic Activity

Synthesis of ordered mesoporous alumina with large pore sizes and hierarchical structure

Direct Synthesis of Titanium Phosphates Functionalized Ordered Mesoporous Materials (SBA-15)

Synthesis of Mesoporous Titania with High Photocatalytic Activity by Nanocrystalline Particle Assembly

Synthesis and Functionalization of Mesoporous Zirconium(Iv) Phosphate-Phenylphosphonate with Small Mesopores

Block Copolymer Templating Syntheses of Ordered Large-Pore Stable Mesoporous Aluminophosphates and Fe-aluminophosphate Based on an “acid–base Pair” Route

Synthesis of ordered small pore mesoporous silicates with tailorable pore structures and sizes by polyoxyethylene alkyl amine surfactant

Synthesis of easily shaped ordered mesoporous titanium-containing silica

Synthesis and characterization of amorphous TiO2 with wormhole-like framework mesostructure

Facile Synthesis for Ordered Mesoporous Gamma-Aluminas with High Thermal Stability

Hydrothermal Synthesis of High Surface Area Mesoporous Lithium Aluminate

Obtaining of Mesoporous Aluminosilicates with High Hydrothermal Stability by Composite Organic Templates: Utility and Mechanism

Development of a simple aqueous solution based chemical method for synthesis of mesoporous γ-alumina powders with disordered pore structure

Synthesis of ordered mesoporous crystalline carbon-anatase composites with high titania contents.

Tetramethylguanidine-templated Synthesis of Aluminophosphate-Based Microporous Crystals with AFI-type Structure

Surface Functionalization of Mesoporous Silica Sba-15 by Liquid-Phase Grafting of Zirconium Phosphate

Hydrothermally Highly Stable Acidic Mesoporous Aluminosilicate Spheres with Radial Channels

Fabrication of High Surface Area Fibrous Tio2 with Well-Defined Mesostructures Via A Nonsurfactant Approach