Abstract:A novel ligand-assisted assembly approach is demonstrated for the synthesis of thermally stable and large-pore ordered mesoporous titanium dioxide with a highly crystalline framework by using diblock copolymer poly(ethylene oxide)-b-polystyrene (PEO-b-PS) as a template and titanium isopropoxide (TIPO) as a precursor. Small-angle X-ray scattering, X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution scanning electron microscopy, and N-2-sorption measurements indicate that the obtained TiO2 materials possess an ordered primary cubic mesostructure with large, uniform pore diameters of about 16.0 nm, and high Brunauer-Emmett-Teller surface areas of -112 m(2) g(-1), as well as high thermal stability (similar to 700 degrees C). High resolution TEM and wide-angle XRD measurements clearly illustrate the high crystallinity of the mesoporous titania with an anatase structure in the pore walls. It is worth mentioning that, in this process, in addition to tetrahydrofuran as a solvent, acetylacetone was employed as a coordination agent to avoid rapid hydrolysis of the titanium precursor. Additionally, stepped evaporation and heating processes were adopted to control the condensation rate and facilitate the assembly of the ordered mesostructure, and ensure the formation of fully polycrystalline anatase titania frameworks without collapse of the mesostructure. By employing the obtained mesoporous and crystallized TiO2 as the photoanode in a dye-sensitized solar cell, a high power-conversion efficiency (5.45%) can be achieved in combination with the N719 dye, which shows that this mesoprous titania is a great potential candidate as a catalyst support for photonic-conversion applications.

Synthesis of Mesoporous Titania with High Photocatalytic Activity by Nanocrystalline Particle Assembly

Soft-chemical Synthesis of Mesoporous Nitrogen-Modified Titania with Superior Photocatalytic Performance under Visible Light Irradiation

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Synthesis, Characterization and Photocatalysis of Mesoporous Tio2

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Synthesis of Nano Titania Particles Embedded in Mesoporous SBA-15: Characterization and Photocatalytic Activity.

Mesoporous titanium dioxide (TiO2) with hierarchically 3D dendrimeric architectures: formation mechanism and highly enhanced photocatalytic activity.

Synthesis and Characterization of Mesoporous TiO2 with Wormhole-Like Framework Structure

Synthetic Route to the Nano-Sized Titania with High Photocatalytic Activity Using a Mixed Structure-Directing Agent

Synthesis of Well-Ordered Mesoporous Titania with Tunable Phase Content and High Photoactivity

Preparation of Mesoporous Anatase Titania with Large Secondary Mesopores and Extraordinarily High Photocatalytic Performances

Hydrothermal Synthesis and Morphological Evolution of Mesoporous Titania−Silica

Synthesis of La3+ doped mesoporous titania with highly crystallized walls

Synthesis of Phosphorus-Doped Titania with Mesoporous Structure and Excellent Photocatalytic Activity

Characterization of Mesoporous Nanocrystalline TiO2 Photocatalysts Synthesized Via a Sol-Solvothermal Process at a Low Temperature

Synthesis of bi-porous TiO2 with crystalline framework using a double surfactant system

Ligand‐Assisted Assembly Approach to Synthesize Large‐Pore Ordered Mesoporous Titania with Thermally Stable and Crystalline Framework

Low Temperature Synthesis of Crystalline Mesoporous Titania with High Photocatalytic Activity by Post-Treatment in Nitric Acid Ethanol Solution

Three-dimensional Interconnected Mesoporous Anatase TiO2 Exhibiting Unique Photocatalytic Performances

Controlled synthesis of ordered mesoporous C-TiO2 nanocomposites with crystalline titania frameworks from organic-inorganic-amphiphilic coassembly

Synthesis and Characterization of Carbon-Modified Titania Photocatalysts with a Hierarchical Meso-/Macroporous Structure.