Abstract:Mesoporous SiO2-modified nanocrystalline TiO2 photocatalysts have been prepared by sol-hydrothermal processes, followed by post-treatment with appropriate amount of surfactant F127-modified silica sol. The resulting photocatalysts were also characterized by X-ray diffraction, Raman spectroscopy, Brunauer-Emmett-Teller spectroscopy, N-2 adsorption-desorption, transmission electron microscopy, FT-IR, X-ray photoelectron spectroscopy, UV-vis diffuse reflectance spectroscopy, steady state surface photovoltage (SS-SPV), and transient state surface photovoltage (TS-SPV) techniques. The photocatalytic activities of the samples were evaluated by degrading rhodamine B solution under simulated solar illumination. The results show that the surface modification with mesoporous SiO2 greatly enhances the thermal stability of the nanocrystalline anatase TiO2, even still being with a main anatase phase after calcination at 900 degrees C, and the more is the amount of SiO2 used, the more obvious is the ehancement in the thermal stability. This enhancement is attributed to the effective inhibition of the direct contacts and the diffusions among anatase nanocrystals as well as to the retardation of the crystallite growth. Interestingly, the proper amount of mesoporous SiO2-modified nanocrystalline TiO2 samples by thermal treatment at high temperature can exhibit much higher photocatalytic activity than the commercial-available P25 TiO2, which is explained mainly by the high photoinduced charge carrier separation rate resulting from the high anatase crystallinity based on the analyses of SS-SPV and TS-SPV responses and the large surface area related to the small nanocrystallite size and mesoporous SiO2 as well as still possessing a certain amount of surface hydroxyl group.

Characterization of Mesoporous Nanocrystalline TiO2 Photocatalysts Synthesized Via a Sol-Solvothermal Process at a Low Temperature

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Low-temperature hydrothermal synthesis of highly photoactive mesoporous spherical TiO2 nanocrystalline

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Solvothermal Growth of Three-Dimensional TiO2 Nanostructures and Their Optical and Photocatalytic Properties

Solvothermal Synthesis of Nanosized Tio2 Particles with Different Crystal Structures and Their Photocatalytic Activities

Study of Photocatalytic Activity of Cd-doped Mesoporous Nanocrystalline TiO 2 Prepared at Low Temperature

Preparation of Controllable Crystalline Titania and Study on the Photocatalytic Properties.

Preparation of NanoTiO2 Photocatalyst Sol

Sol-Gel Preparation and Characterization of High Activity Titanium Dioxide Nanocrystalline Photocatalyst

Mesoporous SiO2-Modified Nanocrystalline TiO2 with High Anatase Thermal Stability and Large Surface Area As Efficient Photocatalyst

Low Temperature Synthesis of Crystalline Mesoporous Titania with High Photocatalytic Activity by Post-Treatment in Nitric Acid Ethanol Solution

Synthesis of Mesoporous Titania with High Photocatalytic Activity by Nanocrystalline Particle Assembly

Synthesis, Characterization and Photocatalysis of Mesoporous Tio2

Photocatalytic activity of TiO 2 prepared at low temperature by a photo-assisted sol-gel method

Mesoporous Tio2 Micro-Nanometer Composite Structure: Synthesis, Optoelectric Properties, and Photocatalytic Selectivity

Preparation of a Highly Active Nanocrystalline TiO2 Photocatalyst from Titanium Oxo Cluster Precursor

Mesoporous Titania (A) Nanoparticles Prepared by a Solvothermally Treated Organic Small Molecule System: Formation Mechanism and Behavior in Photocatalysis and Dye-Sensitized Solar Cells

Preparation at Lower Temperature and Characterization of TiO_2 Sol with Photo-Catalytic Activity

Ultrasonic preparation of mesoporous titanium dioxide nanocrystalline photocatalysts and evaluation of photocatalytic activity