Abstract:Without use of any templates or shape-protectors, uniformly sized anatase TiO2 nanocrystallites with cuboidal morphology were synthesized by changing titanium hydroxide precipitates into their corresponding ethanol-gels (viz. by washing several times with anhydrous ethanol) followed by drying in supercritical ethanol (7.0MPa, 270°C) and calcination at high temperature (AS-preparation). Characterizations with X-ray diffraction (XRD), Raman spectroscopy and nitrogen adsorption suggest that the cuboidal anatase nanocrystallites are highly resistant to thermal sintering. The anatase structure of the cuboidal nanocrystallites was maintained even after calcinations up to temperatures as high as 800°C. Thermogravimetric (TG) measurements in flowing air show that the as-prepared cuboidal TiO2 nanocrystallites were contaminated with some carbonaceous residues, which can be completely removed by calcination at 500°C in air. Application of these cuboidal TiO2 nanocrystallites as photocatalytic materials was evaluated by photocatalytic degradation of methyl orange in water. With increasing the calcination temperature up to 800°C, the photocatalytic activities of anatase TiO2 cuboids increased gradually due to improved crystallization of the material. The sample calcined at 800°C afforded the highest photocatalytic activity, which is comparable to that of the commercial photocatalyst Degussa P-25. Due to the presence of carbonaceous residues after the supercritical drying in the preparation, the samples calcined at temperatures no higher than 400°C showed higher photocatalytic activities than the sample calcined at 500°C. However, further calcination of the sample at 1000°C led to drastic reduction in the photocatalytic activity due to the anatase-to-rutile phase transformation and sintering of the material.

Preparation of a Highly Active Nanocrystalline TiO2 Photocatalyst from Titanium Oxo Cluster Precursor

Preparation of WO<sub>x</sub>-TiO<sub>2</sub> and the Photocatalytic Activity under Visible Irradiation

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Influence of Preparation Method on Morphology and Photocatalysis Activity of Nanostructured TiO2.

Preparation and Photocatalytic Activities of Nanocrystal Titania

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Preparation and Photocatalytic Activity of TiO<sub>2</sub>/Fe<sub>2</sub>O<sub>3 &Lt;/sub>nanocomposite

Preparation of TiO_2 Nanoparticle and Their Photocatalytic Property

Large-Scale Preparation Of Ordered Titania Nanorods With Enhanced Photocatalytic Activity

Preparation of Nanoparticle WO_3-doped TiO_2 and Research on Its Photocatalytic Activity

Preparation and Characterization of Nanosized Anatase TiO2 Cuboids for Photocatalysis

Preparation of high active nanometer TiO2 sonocatalyst by partial transition crystal in hydrogen peroxide solution under ultrasonic irradiation

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Surface roughening and top opening of single crystalline TiO2 nanowires for enhanced photocatalytic activity

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Solvothermal Synthesis of Nanosized Tio2 Particles with Different Crystal Structures and Their Photocatalytic Activities

Highly Active Rutile TiO 2 for Photocatalysis

Nonaqueous sol–gel synthesis and growth mechanism of single crystalline TiO2 nanorods with high photocatalytic activity

Preparation and Characterization of Nano-Tio2 Photocatalysts by Electrolysis Chemistry Method

Preparation of Anatase-Type TiO_2 Nanoparticals from Ti (SO4)2 Solution under Hydrothermal Conditions and Its Photocatalytic Performance

Solvothermal Preparation of Tio2/Montmorillonite and Photocatalytic Activity