Study on relationship of particle structure and photocatalytic properties of nano-TiO2 powder
Xiaohong Tang,Yun Zhang,Guangfu Yin,Dali Zhou,Heng Liu,Changqiong Zheng
DOI: https://doi.org/10.3321/j.issn:1002-185x.2004.08.021
2004-01-01
Rare Metal Materials and Engineering
Abstract:TiO2 powder, particle size less than 10 nm, has been prepared by the hydrolysis of TiOSO4 solution in the presence of a kind of self-made surfactant, and the photocatalytic degradation of methyl orange solution by using nanosized TiO2 has been studied. The results show that nano- TiO2 powder has a much higher photocatalytic activity to the methyl orange solution than that of commercial TiO2, and the degradation rate of methyl orange solution is roughly more than doubled that of the commercial TiO2. Moreover, the microstructures and morphology of the TiO2 powders were characterized by XRD, TEM. It was found that the TiO2 particles appear anatase structure with the size about 5.5 nm similar to 9.6 nm with heating treatment at 400 degreesCsimilar to800 degreesC, and rutile began to appear at 850 degreesC. The amount of rutile and particle size of TiO2 increased with increasing temperature. At 1 100 degreesC the formed nano-TiO2 completely transferred to rutile. The photocatalytic activity of the TiO2 powder depends on the heating treatment temperature and crystal structure. The photocatalytic activity of the nano-TiO2 with ratio of anatase 97.7%(wt ratio) and rutile 2.3% is superior to that of the commercially available nano-TiO2.