Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Direct Synthesis of Titanium Phosphates Functionalized Ordered Mesoporous Materials (SBA-15)

Direct Synthesis of Titanium Substituted SBA-15 under Conventional Hydrothermal Conditions and Their Catalysis Characterization

Direct Synthesis, Characterization and Catalytic Activity of Titanium-Substituted Sba-15 Mesoporous Molecular Sieves

Ordered Mesoporous Titanium Phosphate Material: A Highly Efficient, Robust and Reusable Solid Acid Catalyst for Acetalization of Glycerol

Direct Synthesis and Structural Characteristics of Titanium Dioxide/Mesoporous SBA-15 Materials

TiO2/SBA-15 Photocatalysts Synthesized Through the Surface Acidolysis of Ti(OnBu)4 on Carboxyl-Modified SBA-15

Synthesis and Photocatalytic Activity of Highly Dispersed TiO_2/SBA-15

Synthesis of easily shaped ordered mesoporous titanium-containing silica

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Using phosphoric acid as a catalyst to control the structures of mesoporous titanium dioxide materials

The synthesis of novel hybrid thiol-functionalized nano-structured SBA-15

Synthesis of Well-Ordered Mesoporous Titania with Tunable Phase Content and High Photoactivity

Stable ordered mesoporous titanosilicates with active catalytic sites

Surface Functionalization of Mesoporous Silica Sba-15 by Liquid-Phase Grafting of Zirconium Phosphate

Incorporation of Titanium into Mesoporous Silica Molecular Sieve SBA-15

Layer-by-layer Grafting of Titanium Phosphate Onto Mesoporous Silica SBA-15 Surfaces: Synthesis, Characterization, and Applications.

Direct synthesis of mesoporous TiO2 modified with phosphotungstic acid under template-free condition

Synthesis of Heteroatom Substituted SBA-15 by the “pH-Adjusting” Method

Triphenylphosphine-based functional porous polymer as an efficient heterogeneous catalyst for the synthesis of cyclic carbonates from CO2

Synthesis and characterization of Ti-SBA-16 ordered mesoporous silica composite

Post-Grafting Preparation Of Large-Pore Mesoporous Materials With Localized High Content Titanium Doping