Abstract:The present study reports a simple, template free and controllable one-step synthesis of a series of amorphous, crystalline, and triphasic TiO 2 nanoparticles utilizing titanium( IV ) ethoxide as a molecular precursor. By reacting the titanium ethoxide in a mixture of ethanol, acetic acid, and water at reflux temperatures while varying the ratios of the reaction components, it was possible to obtain TiO 2 nanoparticles possessing high surface areas and pore volumes as well as diverse crystalline structures. The synthesized nanoparticles were characterized by FT-IR, XRD, SEM, TEM, TG, DTA, DTG, DRS, and argon sorption. X-ray diffraction and sorption analyses conclusively show that using an excess of ethanol resulted in the formation of an amorphous TiO 2 with a high surface area. Furthermore, an increase in the water content while slightly reducing the amount of acid but keeping ethanol still at excess resulted in the formation of a crystalline anatase phase, whereas the reaction in the absence of ethanol led to the formation of a triphasic material consisting of anatase (40.5%), rutile (25.5%), and brookite (34%). Under the optimized conditions, it was possible to produce amorphous and crystalline porous titanium dioxide with high surface areas of 350 and 310 m 2 g −1 respectively at low temperatures without subsequent heat treatment, which is reflected in their catalytic properties. Investigation of the photocatalytic and catalytic abilities of the synthesized nanoparticles to degrade and to reduce methylene blue (MB), respectively, as well as reduction of nitroaromatic compounds in aqueous media revealed that the amorphous materials showed the best performance with degradation of up to 94–99% of MB within 10 minutes. The kinetic studies also revealed that all nanoparticles exhibited high catalytic activity for the reduction of MB within a short time (3–4 min) and showed good agreement with a pseudo-first-order reaction model. The derived rate constants for the catalytic reduction of 2-NP, 3-NP, 4-NP, 2-NA, and 3-NA (NP = nitrophenol and NA = nitroaniline) with amorphous TiO 2 nanoparticles ( Ti-9 ), as the best catalyst, are 0.67 min −1 , 0.24 min −1 , 1.46 min −1 , 0.56 min −1 , and 0.21 min −1 , respectively. From the data, we can deduce that a high specific surface area, the occurrence of defects as well as the crystallinity of the materials play an essential role in the photocatalytic and catalytic performance.

Using phosphoric acid as a catalyst to control the structures of mesoporous titanium dioxide materials

Acid-regulated hydrolysis and condensation of titanium cation toward controllable synthesis of multiphase mesoporous TiO2 for effectively enhance photocatalytic H2 evolution

Direct synthesis of mesoporous TiO2 modified with phosphotungstic acid under template-free condition

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Synthesis of Mesoporous TiO2 Materials with High Specific Area Using Inorganic Acids As Catalysts

Controllable Synthesis of Mesoporous TiO2 Polymorphs with Tunable Crystal Structure for Enhanced Photocatalytic H2 Production

Direct synthesis of mesoporous TiO2 and its catalytic performance in DBT oxidative desulfurization

Preparation of porous rutile titania from ilmenite by mechanical activation and subsequent sulfuric acid leaching

Controllable and facile one-pot synthesis of high surface area amorphous, crystalline, and triphasic TiO2: catalytic and photocatalytic applications

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Mesoporous titanium dioxide (TiO2) with hierarchically 3D dendrimeric architectures: formation mechanism and highly enhanced photocatalytic activity.

Effect of the P/Ti Ratio on the Visible-Light Photocatalytic Activity of P-Doped Tio2

Synthesis and Characterization of Mesoporous TiO2 with Wormhole-Like Framework Structure

Mesoporous TiO2 Microspheres with Precisely Controlled Crystallites and Architectures

Synthesis of Well-Ordered Mesoporous Titania with Tunable Phase Content and High Photoactivity

Ligand‐Assisted Assembly Approach to Synthesize Large‐Pore Ordered Mesoporous Titania with Thermally Stable and Crystalline Framework

Role of Phosphorus in Synthesis of Phosphated Mesoporous TiO2 Photocatalytic Materials by EISA Method

Novel Thermally Stable Phosphorus-Doped TiO2 Photocatalyst Synthesized by Hydrolysis of TiCl4

Layer-by-layer Grafting of Titanium Phosphate Onto Mesoporous Silica SBA-15 Surfaces: Synthesis, Characterization, and Applications.

Mesoporous TiO2 Single Crystals: Facile Shape-, Size-, and Phase-Controlled Growth and Efficient Photocatalytic Performance.