Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Preparation of porous rutile titania from ilmenite by mechanical activation and subsequent sulfuric acid leaching

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Preparation and Properties of TiO2/illite Composites Synthesized at Different Hydrothermal Ph Values

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Template-free Hydrothermal Synthesis of Macroporous TiO2 Microspheres on a Large Scale

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

The Effect of Calcination Temperature on the Structure and Activity of TiO2/SiO2 Composite Catalysts Derived from Titanium Sulfate and Fly Ash Acid Sludge

Large-scale Synthesis and Characterization of Fan-Shaped Rutile TiO2 Nanostructures

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

Using phosphoric acid as a catalyst to control the structures of mesoporous titanium dioxide materials

Titanite-Containing Mineral Compositions and Their Chemical Treatment with Preparation of Functional Materials

Preparation and Photocatalytic Properties of Rutile TiO2 from BaTiO3 by Hydrothermal Treatment

The Hydrometallurgical Approach in the Production of a High Content of Titanium Dioxide (TiO2) from Ilmenite, Direct Hydrochloric and Sulfuric Acid Leaching and Pre-Treatment Methods: A Review

Microstructure and phase evolution of TiO2 precursors prepared by peptization-hydrolysis method using polycarboxylic acid as peptizing agent

Preparation and Photocatalytic Properties of Rutile TiO_2 from BaTiO_3 by Hydrothermal Treatment

Acid-regulated hydrolysis and condensation of titanium cation toward controllable synthesis of multiphase mesoporous TiO2 for effectively enhance photocatalytic H2 evolution

Preparation and Characterization of Titania Ion-Sieves

TiO2/SBA-15 Photocatalysts Synthesized Through the Surface Acidolysis of Ti(OnBu)4 on Carboxyl-Modified SBA-15

Preparation of spherical TiO2 from TiOSO4 by hydrolysis