Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Microstructure and phase evolution of TiO2 precursors prepared by peptization-hydrolysis method using polycarboxylic acid as peptizing agent

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

A study on the synthesis of coarse TiO2 powder with controlled particle sizes and morphology via hydrolysis

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

pH control on preparation of nano-TiO_2 by gel-sol process

Effect of Peptization on Phase Transformation of Tio2 Nanoparticles

Preparation and Properties of TiO2/illite Composites Synthesized at Different Hydrothermal Ph Values

Effect of Peptisation on Nanosized TiO2 Particles Prepared by Hydrolysis from Metatitanic Acid

Effect of hydrolysis conditions on morphology and crystallization of nanosized TiO2 powder

Morphology Control of Tio2 Through Hydrothermal Synthesis Method Using Protonic Tetratitanate

Preparation Crystalline Mesoporous Titania at Mild Conditions with Inorganic Titanium Precursors

Preparation of Controllable Crystalline Titania and Study on the Photocatalytic Properties.

The Preparation of Rutile TiO<sub>2</sub> Nanopowders, Phase Transformation and Their Photocatalysed Properties

Tailored preparation of titania with controllable phases of anatase and brookite by an alkalescent hydrothermal route

Preparation of porous rutile titania from ilmenite by mechanical activation and subsequent sulfuric acid leaching

Single- and Mixed-Phase TiO2 Powders Prepared by Excess-Hydrolysis of a Titanium Alkoxide

Preparation and Characterization of Anatase TiO2 Microspheres with Porous Frameworks Via Controlled Hydrolysis of Titanium Alkoxide Followed by Hydrothermal Treatment

Analysis of the structure of titanium tetrachloride derived precipitates

Preparation and investigation of TiO2 Sol containing nanometer anatase crystalline grains

Acid-regulated hydrolysis and condensation of titanium cation toward controllable synthesis of multiphase mesoporous TiO2 for effectively enhance photocatalytic H2 evolution