Effects of Bath Temperature on the Morphology of Zno Nano-Rods and Its Optical Properties

Sumei Zhang,Cailong Yan,Hongxue Zhang,Geyu Lu
DOI: https://doi.org/10.1016/j.matlet.2015.02.050
IF: 3
2015-01-01
Materials Letters
Abstract:ZnO nano-rod arrays with different morphologies were vertically grown on indium-tin oxide (ITO) glass substrates using the electrochemical deposition (ECD) method processing in a two-electrode cell. The bath temperature plays a key role in the growth process. The effect of growth bath temperature was studied with respect to the morphological, structural, and photoluminescence properties of the ZnO nano-rod arrays. The ZnO nano-rod arrays fabricated at 85°C bath temperature had the best morphology, structural and optical qualities. The clear lattice fringes in the image of high-resolution transmission electron microscopy (HRTEM) and X-ray diffraction (XRD) showed that a single-crystal structure of ZnO nano-rods with the growth direction along the [002] direction. The top-sectional field emission scanning electron microscopy (SEM) images results revealed that the bath temperature played a key role in the morphology evolvement of the ZnO nano-rods. A sharp peak in the UV region and a weak broad peak in the visible region between 400 and 500nm were shown in the room temperature photoluminescence (PL) spectra of the samples, suggesting that the ZnO nano-rod arrays with high-quality crystals were obtained. This synthesis method provided a low cost and easy route for the preparation of 1D ZnO nanostructures.
What problem does this paper attempt to address?