Abstract:The polycrystalline IN713C produced via investment casting is one of the widely-used nickel-based superalloy in automotive and aerospace industries. This alloy, however, has an apparent inhomogeneous microstructure generated during casting and contains dendritic structure that gives rise to strain localisation during loading. Yet, the effect of dendrite structure, grain size and shape as well as crystallographic orientation, which directly influence fatigue property and deformation micromechanism in the components, is rarely studied. In the present study, IN713C cast bars are tailored with three different grain structures, i.e., transition, equiaxed and columnar, with substantial grain size variations. The produced bars were tested under strain controlled LCF (Low Cycle Fatigue) and stress controlled HCF (High Cycle Fatigue) conditions at 650 °C. The results showed that most of fatigue cracks initiated from casting porosities and fatigue life extended in the microstructure with a small grain size during both HCF and LCF loadings. It is also demonstrated that fatigue striations were mainly observed within dendrite areas during crack propagation, whereas the higher GND (Geometrically Necessary Dislocation) density were predominantly observed in the interdendrite areas. Here, we propose a concept of 'Crack Propagation Unit (CPU)' for better description of deformation mechanism at local scale during fatigue loading by combining fracture surface characteristic methodology and dislocation distribution analyses within the dendrite structural unit. Furthermore, this model to understand the deformation micromechanism can provide a new perspective on the interpretation of Hall-Petch relationship in casting materials that contain dendritic structure. This is further demonstrated via direct correlation of the high crack propagation resistance with the crack path divergence instead of the dislocation pile-up at the grain boundary or in-between the γ/ γ' channels. Moreover, by utilising serial sectioning method followed by layered EBSD scanning, quasi-3-D grain orientation mappings were obtained, and crystallographic texture information were directly correlated with the fracture surface observations. This allowed an investigation of the influence of orientation of individual grains and micro/macro texture on crack propagation rate. The critical stage of crack propagation in fatigue life and its correlations with microstructural features is established, offering potential practical applications by controlling the investment casting process parameters.

Multiaxial and Non-Proportional Microstructure-Sensitive Fatigue Crack Nucleation

Role of Geometrically Necessary Dislocation Density in Multiaxial and Non-Proportional Fatigue Crack Nucleation

High Cycle Fatigue Life Prediction Model Based on Crystal Plasticity and Continuum Damage Mechanics for Ni-based Single Crystal Superalloys under a Multiaxial Stress State

Microstructurally-sensitive Fatigue Crack Nucleation in Ni-based Single and Oligo Crystals

Thermo-Mechanical Fatigue Constitutive Model for Nickel-Based Single Crystal Superalloys

Multiscale assesment of microstructurally-sensitive fatigue crack nucleation and growth and their mechanistic drivers

Stress Redistribution and Stress Triaxiality Effect on the Fatigue Life of Notched Ni-based Single Crystal Superalloy at 760℃

Fatigue Crack Behaviors under Asynchronous Biaxial Loading

A Low-Cycle Fatigue Life Model of Nickel-Based Single Crystal Superalloys under Multiaxial Stress State

Creep-fatigue Behavior of Nickel-Based Single Crystal Superalloy with Different Orientations: Experimental Characterization and Multi-Scale Simulation

A Crystallographic Model for the Orientation Dependence of Low Cyclic Fatigue Property of a Nickel-Base Single Crystal Superalloy

Quantitative Assessment of Microstructural Damage for Interior Crack Initiation and High Cycle Fatigue Life Modeling

A Crystal Plasticity Phase-Field Model for Microstructure Sensitive Fatigue Crack Growth in a Superalloy

Fatigue Life and Mechanistic Modeling of Interior Micro-Defect Induced Cracking in High Cycle and Very High Cycle Regimes

Multi-axial Fatigue Life Assessment of Additively Manufactured Nickel-Based Superalloys

Experimental Estimation of the Probability Distribution of Fatigue Crack Growth Lives

Multiscale Mechanical Fatigue Damage of Stainless Steel Investigated by Neutron Diffraction and X-ray Microdiffraction

The Effects of Grain Size, Dendritic Structure and Crystallographic Orientation on Fatigue Crack Propagation in IN713C Nickel-Based Superalloy

Molecular Dynamics Study of Fatigue Behavior of Nickel Single-Crystal under Cyclic Shear Deformation and Hyper-Gravity Condition

An Experimental Methodology for Quantitative Characterization of Multi-Site Fatigue Crack Nucleation in High-Strength Al Alloys

On multiaxial creep–fatigue considering the non-proportional loading effect: Constitutive modeling, deformation mechanism, and life prediction