Abstract:ABSTRACTCompared with poly(butylene terephthalate)/glycidyl methacrylate grafted poly(ethylene–octene) (PBT/POE‐g‐GMA) binary blends, supertough PBT‐based ternary blends with little rigidity loss were successfully obtained by adding rigid polypropylene (PP) into PBT/POE‐g‐GMA blends to construct core–shell particles during melt blending. The effects of PP content and type on the phase morphology and mechanical properties of the blends were systematically investigated. Theoretical predictions and scanning electron microscopy observation showed that a core–shell structure was formed in PBT matrix with PP as the core and POE‐g‐GMA as the shell. The mechanical property tests showed that POE‐g‐GMA and PP had significant synergistic toughening effect. When PP with high melt flow index (H‐PP) was used, PBT/POE‐g‐GMA/H‐PP (70/15/15) blends possessed the highest Izod notched impact strength, which was 1.9‐fold compared with PBT/POE‐g‐GMA (70/30) binary blends, while the tensile performance loss was little. The essential work of fracture tests was performed to evaluate the fracture resistance of different samples. The results demonstrated that PBT/POE‐g‐GMA/PP ternary blends possessed much better resistance to crack propagation than PBT/POE‐g‐GMA binary blends. The decrease of interparticle distance and the fibrillation of core–shell particles activated intense matrix shear yielding, which was the reason for the high crack resistance of ternary blends. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020, 137, 48872.

Effect of Nucleating Agent on the Structure and Properties of Polypropylene/Poly(Ethylene-Octene) Blends

Research on Toughening Modification of Copolymerized Polypropylene Using Polyolefin Elastomers

Study on Synergistic Toughening Polypropylene by Combining of β-nucleating Agent and Ethylene-octene Copolymer Elastomer

Preparation of PBT/POE‐g‐GMA/PP Ternary Blends with Good Rigidity–toughness Balance by Core–shell Particles

Toughening of PBT by POE/POE-g-GMA Elastomer Through Regulating Interfacial Adhesion and Toughening Mechanism

Effect of Morphology Development on the Low‐temperature Tensile Properties of PP / POE Blends

Morphology, rheology, and mechanical properties of polylactide/ poly(ethylene-co-octene) blends

Fracture behavior and deformation mechanism of polypropylene/ethylene-octene copolymer/magnesium hydroxide ternary phase composites

Relationship between structure and properties in high-performance PA6/SEBS-g-MA/(PPO/PS) blends: The role of PPO and PS

The effect of elastomeric nano-particles on the mechanical properties and crystallization behavior of polypropylene

Modification of Polypropylene with Composite Nucleating Agents Containing 2,2-Methylene-bis-(4, 6-di-t-butylphenylene) Phosphate/Attapulgite/Silica Nano-particles

Synergistic toughening effects of elastomer toughener and nucleating agent on mechanical properties and crystallization behaviors of polypropylene

Effect of nucleating agents on crystalline morphology and mechanical properties of polypropylene

Toughening Effects of "Core-Shell" Particles in PA6/SEBS-g-MA/PPO Blends

Realizing Simultaneous High‐temperature Strength and Low‐temperature Elongation in Polyolefin Elastomer Toughened Polypropylene Via Controlling the Dispersed Phase Size

Preparation of Poly(Phenylene Oxide)/Polyamide-6 Nanocomposites with High Tensile Strength and Excellent Impact Performance

Preparation and Properties of Ethylene Octane Copolymer Blends with High Strength and Polarity

Effectively toughening polypropylene with in situ formation of core-shell starch-based particles

Effects of nucleating agents and extractants on the structure of polypropylene microporous membranes via thermally induced phase separation

Effects of Α and Β Nucleating Agent Compounds on Properties of Polypropylene

Synergistic Toughening Effect of Olefin Block Copolymer and Highly Effective Β-Nucleating Agent on the Low-Temperature Toughness of Polypropylene Random Copolymer