Formation Mechanism of NSA of Secondly Nano Self-Assembly Macropore Alumina Penetrable Pore

Wang Shuang,Ding Wei,Wang Ding-Cong,Zhao De-Zhi

DOI: https://doi.org/10.11862/CJIC.2015.214

2015-01-01

Chinese journal of inorganic chemistry

Abstract:The macropore alumina catalysis material FA-06 was prepared by nano self-assembly technique which has a pore volume of 1.39 cm(3).g(-1), a specific surface area of 297 m(2).g(-1), most probable pore size of 32.4 nm and a porosity of 81.85%. High concentration pore size distribution of 10 similar to 30 nm and 30 similar to 60 nm which percentages are 35.61% and 40.88%, respectively. GPC showed that the dispersion and relative molecular weight of RHP are controlled by the amount of PIBSA, which is the formation material of RHP, in order to control the pore sizes. From TEM and SEM, the results showed that the diameters of nano aluminum hydroxide rods are 250 similar to 300 urn, and the lengths are 600 similar to 800 nm. After calcinating at 550.0 degrees C, the nano alumina rods had the diameter of 150 similar to 300 urn, the length of 400 similar to 600 nm. XRD results of burned nano self-assembly aluminum hydroxide showed that gamma-Al2O3 be formed completely from three types of precursor of nano self-assembly aluminum hydroxide by burning process. Combining with data of TG, the gamma-Al2O3 is folioed completely due to the decomposition of pseudoboehmite at temperature of 605.0 degrees C, and the total weight loss reaches 61.88%. Based on the above experimental results, the molecular self-assembly and nano self-assembly formation process of reverse supersoluble micelle, aluminum hydroxide and macropore alumina were simulated. Moreover, the formation mechanism of NSA of nano self-assembly macropore alumina with penetrable pores was presented.