Study on Lf Refining Slag and Slagging Regime of High-Aluminium Steel

Zeng Jian-hua,Zhang Min,Chen Yong,He Sheng-ping,Wang Qian

DOI: https://doi.org/10.13228/j.boyuan.issn1006-706x.2011.s2.033

2011-01-01

Journal of Iron and Steel Research International

Abstract:During secondary refining of molten steel, reaction of steel–slag has great influence on the quality of steel. Taking high aluminium steel ([Al]≥0.8%) for instance, reaction control of 4[Al]+3(SiO2) = 2(Al2O3)+3[Si] was discussed by both thermodynamics calculation and industrial experiments. The results show that content of silicon increased sharply when content of SiO2 in slag exceeded 10%. In order to prevent the increment of silicon content and reoxidation for high aluminium steel, reasonable component range of LF refining slag is: %CaO/%Al2O3=1.6-1.9, %SiO2 10. Results of the industrial experiments indicate that the CaO-Al2O3 based refining slag has strong ability of desulfurization and inclusion absorption. Average desulfurization rate is 80%, and T[O] reduces above 50% after refining, with the average sulfur content and T[O] about 0.0025% and 11×10-6,respectively, which can meet the requirements of secondary refining and obtain good castability of steel in continuous casting process.