Abstract:Background: With the continuous application of API 5L X100 high-strength grade steel pipeline and the development trend of increasing pipeline diameter and design pressure in China's long natural gas and petroleum pipeline, API 5L X100 high-strength grade steel pipeline steel is bound to become the aorta in long-distance pipeline construction in the future. Studying the failure pressure of API 5L X100 high-strength grade steel pipeline has high economic and social benefits Objective: Exploring the corrosion mechanism of the two single corroded pipeline models with outer defect and inner defect. objective: Using ANSYS Workbench 15.0 software to explore the two single corroded piping models with outer defect and inner defect. Methods: Using ANSYS Workbench 15.0 software to explore the two single corroded pipeline models with outer defect and inner defect and the influence of geometric parameters such as defect depth, defect length, defect width, etc., on the maximum equivalent stress and failure pressure investigated. Based on the finite element analysis database, the failure pressures of two single corroded pipeline models were fitted using Matlab software and the fitting formulas. Results: In the corrosion defect area of the pipeline, stress concentration occurs; Far away from the corrosion defect area, the stress distribution is uniform. For the pipeline model with outer defect and inner defect, as the defect depth and length increases, failure pressure shows a decreasing trend and is almost unaffected by defect width; As the ratio of diameter to thickness increases, failure pressure shows a decreasing trend; By fitting failure pressure formula of the pipeline models with outer defect and inner defect, a multivariate fitting function formula of failure pressure is obtained, with high fitting exactitude. Conclusion: The conclusion obtained have certain guiding values for the normal and stable operation of natural gas and petroleum transportation pipelines.

Research on root morphology regularization method of incomplete penetration defect in pressure pipe

Research On Safety Assessment Method For Pressure Pipe With Incomplete Welding Defects Under Complicated Loadings

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Plastic Limit Load Analysis for Pressure Pipe with Incomplete Welding Defects Based on the Extended Net Section Collapse Criteria

Safety Test Research of Pressure Pipes Containing Incomplete Welding Defects

Numerical Study of CFRP-Bonded Pressure Pipes Subject to Impact Load

Plastic Limit Load Analysis of Pressure Pipes Containing Incomplete Welding Defects under Combined Loadings

Mismatch effect on safety assessment of pressure pipe with incomplete penetration defect

Safety analysis of pressure piping containing incomplete penetration under combined loads

New evaluation method of failure pressure of steel pipeline with irregular-shaped defect

On Elastic-Plastic Collapse of Subsea Pipelines under External Hydrostatic Pressure and Denting Force

Study on safety evaluation method of incomplete penetration welded pipeline under combined loads of internal pressure and bending moment

Safety assessment of incomplete penetration defects at the root of girth welds in pipelines

Elastic Buckling of Cylindrical Pipe Linings with Variable Thickness Encased in Rigid Host Pipes

On the Collapse Failure of Dented Pipes under Bending Moment and External Pressure

INVESTIGATION ON PLASTIC FAILURE LOAD OF PIPING BRANCH JUNCTIONS WITH CIRCUMFERENTIAL CRACKS

The Effect of Pipeline Root Weld Microstructure on Crack Growth Behaviour

Research on the Deformation Characteristics of Pressure Culvert Linings Based on Monitoring

Research on Failure Pressure of API 5L X100 Pipeline with Single Defect

On the collapse of thick-walled steel pipes under coupling initial geometric imperfection and corrosion defect

Experimental Verification on Limit Load Estimation Method for Pipes with an Arbitrary Shaped Circumferential Surface Flaw