Abstract:Direct ink writing (DIW) and low-temperature sintering methods were applied to prepare Si2N2O-Si3N4 ceramics for radome materials. Lattices of Si-SiO2 green body were printed by DIW with 78 wt % solid portion of water-based Si-SiO2 slurry, in which silicon particles and silica fume were used as the solid portion and Methylcellulose (HPMC) was used as the dispersant. Effects of HPMC addition on stability and silica fume content on rheological properties of the slurry were studied, respectively. The pseudoplastic mechanism of the slurry was analyzed. The Si-SiO2 green bodies were sintered at 1250 °C–1400 °C in nitrogen. The effect of temperature on phase composition, microstructure, mechanical and dielectric properties of samples was investigated. With the HPMC addition of 0.12 wt% and the silica fume proportion of 30 wt% in solid portion, a stable and pseudoplastic slurry with the yield stress of 110.9 Pa was obtained, which is suitable for DIW. With the decrease of initial holding temperature, more N2 enters the sample and reacts with silicon and silica fume, promoting the generation of Si2N2O and Si3N4. The optimal condition yields Si2N2O-Si3N4 ceramics with apparent porosity of 42.73%, compressive strength of 24.7 MPa, dielectric constant of 4.89 and loss tangent of 0.0054. It is found that columnar Si3N4 comes from a direct reaction between silicon and N2, and fibrous Si2N2O is mainly generated by the reaction between silicon, SiO(g), and N2 through the chemical vapor deposition mechanism. Good dielectric properties are achieved due to high porosity, high proportion of Si2N2O phase and no residual silicon.

Direct ink writing of Si<sub>2</sub>N<sub>2</sub>O porous ceramic strengthened by directional -Si<sub>3</sub>N<sub>4</sub> grains

Direct ink writing of Si2N2O porous ceramic strengthened by directional β-Si3N4 grains

Mechanical and Dielectric Properties of Direct Ink Writing Si2N2O Composites

Fabrication and Properties of Embedded Dense Coating on Direct Ink Writing Si2N2O Porous Ceramics

3D Printing of Porous Si2N2O Ceramics Based on Strengthened Green Bodies Fabricated Via Strong Colloidal Gel

Fabrication and properties of Si2N2O-Si3N4 ceramics via direct ink writing and low-temperature sintering

Fabrication of Si 2 N 2 O Ceramic Foam by Combination of Direct Ink Writing and Biological Foaming Technique

Mechanical and Dielectric Properties of 3D Printed Highly Porous Ceramics Fabricated Via Stable and Durable Gel Ink

Direct ink writing additive manufacturing of porous alumina-based ceramic cores modified with nanosized MgO

Morphology Design of Porous Si2N2O Ceramics via Silica Poly-Hollow Microspheres

Direct ink writing of hierarchically porous Al 2 O 3 matrix composites with enhanced wettability of Al

Direct Ink Writing of Continuous SiO 2 Fiber Reinforced Wave-Transparent Ceramics

Microstructures, Mechanical Properties and Electromagnetic Wave Absorption Performance of Porous SiC Ceramics by Direct Foaming Combined with Direct-Ink-Writing-Based 3D Printing

Direct Ink Writing Core-Shell Wollastonite@Diopside Scaffolds with Tailorable Shell Micropores Favorable for Optimizing Physicochemical and Biodegradation Properties

Study on microstructure and mechanical properties of porous Si3N4 ceramics

Effect Of Beta-Si3n4 Initial Powder Size On Texture Development Of Porous Si3n4 Ceramics Prepared By Gel-Casting In A Magnetic Field

Fabrication And Properties Of Porous Si3n4-Sio2 Ceramics With Dense Surface And Gradient Pore Distribution

Fabrication of directional SiC porous ceramics using Fe 2O 3 as pore-forming agent

Simultaneous improvement in porosity and strength of porous β-Si3N4 ceramics by formation of ultrafine fibrous grains

Additive manufacturing of SiC-Sialon refractory with excellent properties by direct ink writing

Study on Microstructure and Mechanical Properties of Porous Si<sub>3</sub>N<sub>4</sub> Ceramics