Abstract:Sri Lanka is a major global producer of raw material-heavy minerals from beach placer deposits. This study focusses on upgrading Sri Lankan ilmenite sands to synthetic rutile via a mechanochemical method. Ball milling-induced sulphurisation and carbothermic reductions were examined using several geochemical techniques. Raw ilmenite concentrate contained over 95 wt% FeTiO3, ∼2 wt% SiO2, and ∼ 1 wt% Al2O3. Ilmenite was mixed with additives (i.e. sulphur, vein graphite, and a 1:1 mix of sulphur and vein graphite), separately in three ratios by weight, namely 1:1, 2:1 and 4:1, respectively. Each mixture was milled for 4 and 6 h. A high percentage of ilmenite/sulphur + graphite (ISG) was converted to nanoparticles (average particle size = 124 nm) in samples milled for 6 h. X-ray diffraction (XRD) spectra indicate that the intensities of sulphur and graphite peaks decrease after ball milling. This suggests possible dissolution of sulphur and graphite into the ilmenite structure, with the formation of mixed composite structures. The optimum ilmenite to additives ratio for ilmenite to rutile conversion was found to be 4:1. The occurrence of pyrite and pseudorutile peaks in XRD spectra of milled samples indicates that ilmenite reduction was initiated during ball milling. Fourier-transform infrared (FTIR) spectra of milled samples confirm the octahedral metal-ion stretching vibrations of carbon-incorporated ilmenite structures. The ilmenite-additive mixtures containing both sulphur and graphite (ISG) showed the best results. Consequently, ISG samples (mixing ratio of 4:0.5:0.5, and milled for 6 h) were isothermally annealed at 800 °C, 1000 °C and 1200 °C, respectively. Sharpening of rutile peaks and disappearance of pyrrhotite peaks in the annealed samples indicated the completion of the mechanochemical reactions that were initiated during ball milling. The optimum temperature for ilmenite reduction was determined to be 1000 °C. At that temperature pseudorutile peaks had disappeared from the XRD spectra of the annealed samples, whereas brookite and rutile peaks appeared. The method introduced in this study thus can be utilised to convert ilmenite to synthetic rutile.

Upgrading ilmenite by an oxidation-magnetic separation-pressure leaching process

Upgrading ilmenite into a high-grade synthetic rutile

Production of synthetic rutile from tin ore beneficiation byproduct through preoxidation and reductive leaching in hydrochloric acid

Research on the process and mechanism of preparing titanium-rich materials from complex ilmenite

Enhancement of ilmenite magnetic properties by oxidation roasting and magnetic separation

A process for producing synthetic rutile from Panzhihua titanium slag

Processing of ilmenite into synthetic rutile using ball milling induced sulphurisation and carbothermic reduction

Thermodynamic Justification for the Effectiveness of the Oxidation—Soda Conversion of Ilmenite Concentrates

Aeration Leaching Process for Producing Synthetic Rutile in a Novel Gas–Liquid–Solid Reactor

A Novel Technology for the Refinement of Low-Grade Ilmenite Concentrate

A Processing Experimental Research of a Rutile Ore

Study on Mineral Processing of A Refractory Low Grade Ilmenite Ore

High-Titanium Slag Preparation Process by Carbothermic Reduction of Ilmenite and Wet-Magnetic Separation

A Novel Process for Titanium Sand by Magnetic Separation and Gravity Concentration

Processing of Ilmenite Concentrate with High Chromium Content

Fundamental Study on Utilization of Titanium Resources by RHF Process

A literature review of titanium metallurgical processes

Gravity Separation Tests of a Complex Rutile Ore

Studies on the Processing of Fine Dusts from the Electric Smelting of Ilmenite Concentrates to Obtain Titanium Dioxide

Mechanism of strengthening consolidation and reduction of ilmenite pellets through high-pressure grinding rolls pretreatment

Recovery of niobium and titanium from ilmenorutile by NaOH roasting-H2SO4 leaching process