Study on Under-Deposit Corrosion Behavior of X65 Steel in Simulated CO2 Saturated Produced Water
Liang Guo,Ping Chen,Chao Huang,Jianqiang Zhang,Yan Xue,Xinran Zhang,Jiayi Tang,Shuliang Wang,Hu Wang
DOI: https://doi.org/10.1016/j.ijoes.2024.100731
IF: 1.541
2024-01-01
International Journal of Electrochemical Science
Abstract:Under-deposit corrosion is a key issue in various processes of oil and natural gas production. In this paper, the corrosion behavior of X65 steel under CaCO3 scales was investigated, which are commonly occurred in such environments. To simulate different conditions of CaCO3 scaling, accelerated scaling was achieved through cathodic polarization on X65 steel samples. Subsequently, chemical immersion of weight loss test was performed over 72h in a simulated produced water at 40°C with a CO2 partial pressure of 0.5MPa (total pressure of 1MPa). The results indicated that pre-scaling duration significantly influenced the corrosion rate of X65 steel. Notably, samples scaled for 6h exhibited a corrosion rate of 0.1572mm/a, markedly higher than 0.0371mm/a of unscaled samples. High-temperature and high-pressure in situ electrochemical measurements were carried out to reveal the electrochemical behavior of X65 steel with varying pre-scaling time, including open circuit potential, linear polarization resistance, electrochemical impedance spectroscopy and polarization curves. Additionally, scanning electron microscopy was used to observe the surface morphology and cross-sectional microstructures before and after product layer removal, which facilitates a discussion on the mechanisms of under-deposit corrosion.