Abstract:Since the period required for testing the atmospheric corrosion of steel is long, most studies have focused on the corrosion behavior in less than three years, making exploring long-term atmospheric corrosion particularly valuable. This study investigates the corrosion behaviors, corrosion models, and mechanical properties of Q235 welded steel pipes collapsing due to corrosion after 25-year service in an urban industrial atmospheric environment using SEM, XRD, electrochemical methods, 3-D noncontact surface profilometry, and static tensile testing. The typical morphologies of & alpha;-FeOOH, & gamma;-FeOOH, and Fe3O4 and the effect of the content of various corrosive materials on the corrosion rate of the steel pipes are identified and analyzed. Then, the influence of different corrosion degrees on the mechanical properties of the steel pipes is examined by considering the morphologies of the rust pits. The results show that the wetting-drying cycles affect the structures of the rust layers and their protective properties. The rust layers on the sheltered surface are thicker but less protective than those on the exposed surface. In the wet state, FeSO4 accelerates ion transfer, while Fe3O4 facilitates electron transfer. These processes collectively contribute to the corrosion of Q235 steel. Moreover, as the time-of-wetness of the rust layers on sheltered specimens increases, the corrosion rate of Q235 steel also accelerates. The corrosion model combines pitting and uniform corrosion and gradually changes from predominated by pitting to thickness as the corrosion degree increases. The corrosion morphology impacts the mechanical properties of the welded steel pipes, and the influences of the thickness loss and maximum rust pit depth on these properties are profound.

Electrochemical Corrosion of the Pipe Body of a J55 Steel by the Electric Resistance Welding

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Corrosion Behavior of J55 Steel in Oilfield Water

Electrochemical Corrosion Behavior of X80 Pipeline Steel in Simulated Solution of Northwest Saline Soil

Erosion–Corrosion Behavior of Friction Stud Welded Joints of X65 Pipelines in Simulated Seawater under Different Flow Rates

Identification of the Selective Corrosion Existing at the Seam Weld of Electric Resistance-Welded Pipes

Electrochemical Corrosion Behavior of X80 Pipeline Steel in Simulated Medium of Saline-alkali Soil

Pitting Corrosion Resistance of Welded Joints of a Super-duplex Stainless Steel by Electrochemical Characteristics Analysis

STUDY OF THE X70 PIPELINE STEEL CORRODING IN 3.0wt% NaCl SOLUTION USING ELECTROCHEMICAL IMPEDANCESPECTROSCOPY TECHNIQUE

Multiscale characterization of seawater pipe erosion of B10 copper-nickel alloy welded joints

Study on Corrosion Behavior of X80 Pipeline Steel in 5%NaCl+0.5% Acetum

Effect of Residual Stress on Electrochemistry Corrosion Resistance of X80 UOE Pipe

On-Line Measurement and Characterization of Electrochemical Corrosion of 304L Stainless Steel Pipe Wall in High-Speed Cl-Containing Solution

Evaluation of corrosion and erosion–corrosion behavior of X65 pipeline steel in flowing CO2-saturated electrolyte

Corrosion behavior of riveted joints with electrophoretic treatment in neutral salt spray environment

Probing the Anti-Corrosion Behavior of X65 Steel Underwater FSW Joint in Simulated Seawater

Electrochemical Corrosion Behaviors of 316 L Stainless Steel Used in PWR Primary Pipes

Corrosion behaviour of 316L stainless steel and anti-corrosion materials in a high acidified chloride solution

Corrosion Behaviors of Metal End of PHC Pipe Pile in Simulated Soil Solutions

Corrosion Behavior of the Steel Used As a Huge Storage Tank in Seawater

GROOVING CORROSION PROPERTIES OF ELECTRIC RESISTANCE WELDED OIL WELL CASING OF J55 STEEL