Abstract:Intermittent contact alternating current scanning electrochemical microscopy (IC-AC–SECM) has been used in the present study to image the local electrochemical activity of Zr-4–Ti–304 L SS dissimilar weld joint without a redox mediator at an open circuit potential. The perturbation frequency and bias potential applied to the Pt ultramicroelectrode (UME) are found to affect the contrast of IC-AC-SECM imaging. The optimum parameters for high contrast imaging with high sensitivity were determined by performing potentiodynamic polarization and approach curves of Pt UME. The potentiodynamic polarization behaviour of Pt UME carried out in tap water revealed that the Pt UME biased with potential at –0.5 V was ideal for obtaining better sensitivity due to the maximum reduction of dissolved oxygen in the electrolyte. The effect of applied perturbation frequencies on Pt UME examined by the approach curves using the AC-SECM technique showed a transition from negative to positive feedback over 304 L SS at about 10 kHz whereas for Zr-4 and Ti the transition was observed at 50 kHz but with only a minor difference in their feedback. Better contrast in mapping local current and impedance magnitude across the weld joint has been achieved by applying an optimum dc bias (–0.5 V) to the Pt tip and perturbation frequency (10 kHz). The IC-AC-SECM results have been compared with the conventional potentiodynamic polarization and electrochemical impedance spectroscopy results of Zr-4, Ti, 304 L SS and the weldment in tap water, where the weld sample undergoes preferential corrosion of 304 L SS region due to the galvanic coupling. The present work provides new insight into the optimal IC-AC-SECM parameters for best lateral imaging to map electrochemical activity with good contrast across a multilayer weld joint in tap water.

Identification of the Selective Corrosion Existing at the Seam Weld of Electric Resistance-Welded Pipes

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Electrochemical Corrosion of the Pipe Body of a J55 Steel by the Electric Resistance Welding

Corrosion Behavior of High Strength Steel Welded Joint in Seawater: A Combinatorial Study Based on General and Localized Electrochemical Methods

Multiscale characterization of seawater pipe erosion of B10 copper-nickel alloy welded joints

Understanding the Effect of Corrosion Resistance in Welded AA2198‐T8 Alloy: Microstructural‐Electrochemical Insights

Corrosion behaviour of 316L stainless steel and anti-corrosion materials in a high acidified chloride solution

Pitting Corrosion Resistance of Welded Joints of a Super-duplex Stainless Steel by Electrochemical Characteristics Analysis

Characterization of Flow-Accelerated-corrosion of Pressure Piping Welded Joints

Erosion–Corrosion Behavior of Friction Stud Welded Joints of X65 Pipelines in Simulated Seawater under Different Flow Rates

Correlation between the microstructure and corrosion behaviour of copper/316 L stainless-steel dissimilar-metal welded joints

Decoupling the role of microstructure and geometric discontinuity introduced by weld reinforcement height on corrosion behavior of SA106B/316L SS welded joint in the flowing 0.5 M NaCl solution

Flow-Accelerated Corrosion Damage in a Steam Pipe Girth Weld

Localized Depth of Galvanic Corrosion at Dissimilar Metal Welding A508/Inconel 182/316L

On-Line Measurement and Characterization of Electrochemical Corrosion of 304L Stainless Steel Pipe Wall in High-Speed Cl-Containing Solution

Corrosion studies using potentiodynamic and EIS electrochemical techniques of welded lean duplex stainless steel UNS S82441

High contrast corrosion mapping of dissimilar metal weld joints using alternating current scanning electrochemical microscopy: A case study with Zr-4–Ti–304L SS weld

Galvanic corrosion of AA5052/304SS welded joint with Zn-based filler metal in marine engineering

Effect of Microstructure Evolution on Corrosion Behavior of Friction Stir Welded Joint for 2195-T8 Alloy

Corrosion behavior of the weld joint of X80 pipeline steel in an acidic red soil

Insight into the corrosion susceptibility and failure mechanism of Cu-Ni alloy pipeline welded joints in simulated marine environment