Abstract:The phase equilibrium of Mg-Cu-Ca ternary system at 350 degrees C were investigated using thirteen key samples. Scanning electron microscopy (SEM) equipped with energy-dispersive spectroscope (EDS) was employed to investigate equilibrium relationships and phase compositions in alloy samples. Powder X-ray diffraction (XRD) technique was used to analyze the crystal structures of new found phases. Two unreported ternary phases, P1 and Mg25-xCu75Cax were observed and investigated for the first time. The compound P1 has a narrow solid homogeneity ranged from about Mg25Cu35Ca40 to Mg30Cu30Ca40 (in at. %). The solid solubility limit of the compound Mg25-xCu75Cax was found to be 8.03 <= x(Ca) <= 16.67 with constant value of about 75 at. % Cu at 350 degrees C. The 2q of fourteen diffraction peaks of new phase P1 were determined to be 23.0 degrees, 35.9 degrees, 37.3 degrees, 38.9 degrees, 42 degrees, 44 degrees, 47 degrees, 52.5 degrees, 54 degrees, 56.7 degrees, 62.3 degrees, 66.8 degrees, 68.2 degrees and 75.4 degrees. The 2q of ten diffraction peaks of the new compound Mg25-xCu75Cax were confirmed to be 20.5 degrees, 21.2 degrees, 34.7 degrees, 35.7 degrees, 42.3 degrees, 43.3 degrees, 44.8 degrees, 47.3 degrees, 50.5 degrees and 74.5 degrees. The maximum solid solubility of Ca in the terminal compound MgCu2 was found to be 8.83 at. % at 350 degrees C. Ternary maximum solid solubility of binary terminal compounds Mg2Ca, Mg2Cu, Cu5Ca and CuCa were less than 2 at. %. In addition, eight three-phase equilibrium relationships were determined in the present work. (C) 2019 Elsevier B.V. All rights reserved.

Phase Equilibria and Crystal Structure of Ternary Compounds in Al-rich Corner of Al-Er-Y System at 673 and 873 K

Solidification paths and phase equilibria at 873 and 673 K in the Al-Er-Zr system

Phase Relationships in the Al-rich Region of the Al-Y-Zr System

Measurement of the phase equilibria in the Al–Zr–Y system at 673 and 823 K

Experimental determination and thermodynamic calculation of phase equilibria in Ag-Zr-Y system

Phase equilibria in Co−Al−Re ternary system at 1100 and 1300 °C

Isothermal Section of the Al2O3–TiO2–Er2O3 Phase Diagram at 1400°C

Phase relationship of the Ag–Zr–Cr system at 1000 and 750°C

Nucleation of L12-Al3M (M = Sc, Er, Y, Zr) Nanophases in Aluminum Alloys: A First-Principles ThermodynamicsStudy

Phase Relationship Of The Ag-Z-Cr System At 1000 And 750 Degrees C

First-Principle Investigation of the Interface Properties of the Core-Shelled L12-Al3M (M = Sc, Zr, Er, Y) Phase

The Thermal Properties of L12 Phases in Aluminum Enhanced by Alloying Elements

Formation and Relative Stabilities of Core-Shelled L12-Phase Nano-structures in Dilute Al–Sc–Er Alloys

Phase equilibria thermodynamics and solidified microstructure in the Ag-Cr-Zr system

Experimental Determination of the Phase Equilibrium in the Mg–Cu–Ca Ternary System at 350 °C

Phase Equilibria, Thermodynamics and Solidified Microstructure in the Copper–Zirconium–Yttrium System

Experimental study on phase relations in the Al-Mo-Nb ternary system

Thermodynamic description of the Al–Ag–Zr system and discovery of the high-strength ternary phase Al1.84Ag0.16Zr

Phase equilibria in Co-Ti-Re ternary system

Experimental determination of the phase equilibria of aluminum-rich Al−Li−Cu alloys

New Insights into Solidification and Phase Equilibria in the Al-Al3Zr System: Theoretical and Experimental Investigations