Abstract:In this paper, the confinement performance and stress–strain response of reinforced concrete (RC) with corroded reinforcement were studied, with consideration given to such key parameters as corrosion levels, size effect, stirrup configurations, and effects of synchronized corrosion of the stirrups and longitudinal reinforcements. A total of 29 square RC columns, which had been corroded through accelerated corrosion tests, were examined using axial compression evaluations. The theoretical corrosion levels of the stirrups ranged from 0% to 20%. The column size coefficient (defined as the volume ratio of the corroded columns to the standard prism) varied from 1.0 to 4.17, and the spacings of the stirrups ranged between 50 mm and 125 mm. The test results revealed that the confinement behaviors were significantly affected by the severity of the corrosion of the stirrups, including the failure mode, bearing capacity, and deformability. The highest reductions in load and displacement ductility were found at a theoretical corrosion level of 20%, up to 22.37% and 77.05%, respectively. Meanwhile, the confinement performance was also found to be influenced by the stirrup spacings and specimen sizes. It was found that although the corrosion of stirrup was much higher than that of longitudinal reinforcement, the corrosion of longitudinal reinforcement would still less affect the compressive performance of the RC column. The semiempirical and semi-theoretical formulas for calculating the compressive strength and corresponding strain were proposed based on the experimental data and theoretical analysis results. Then, an optimal stress–strain prediction model for concrete confined with corroded stirrups was successfully established. The proposed model showed a good correlation with the experimental data when compared with the existing prediction model.

Short-term Load–deflection Behavior of Corroded RC Beams with Confinement Effect Based on the Partial-Interaction Segmental Approach

Numerical Simulation of Partial-Interaction Load-Deflection Behavior of Corroded Reinforced Concrete Beams Based on a Segmental Approach and Evaluation of Reinforcement Corrosion Level

Developing a Three-Dimensional Finite Element Analysis Approach to Simulate Corrosion-Induced Concrete Cracking in Reinforced Concrete Beams

Effects of Stirrups on Bond Behavior Between Concrete and Corroded Steel Bars

Study of the confinement performance and stress-strain response of RC columns with corroded stirrups

Corrosion-induced Shear Performance Degradation of Reinforced Concrete Beams

Deflection and Crack Calculation of Corroded Reinforced Concrete Beams

Shear Performance of Reinforced Concrete Beams with Corroded Stirrups in Chloride Environment

Effect of Corrosion on Bond Behavior and Bending Strength of Reinforced Concrete Beams

FLEXURAL CAPACITY OF CORROSION-DAMAGED RC BEAMS

Performance of Reinforced Concrete Beams Corroded under Sustained Service Loads: A Comparative Study of Two Accelerated Corrosion Techniques

Study on Degradation Regularity of Bearing Capacity of RC Beams under Corrosive Conditions

Crack Propagation and Flexural Behaviour of Rc Beams under Simultaneous Sustained Loading and Steel Corrosion

Experimental Analysis of Corroded RC Continuous Beams Rehabilitated by ICCP-SS under Unsymmetrical Loading

The influence of longitudinal rebar type and stirrup ratio on the bond performance of reinforced concrete with corrosion

CFRP Strengthened RC Beams with Pre-Strengthening Non-Uniform Reinforcement Corrosion Subjected to Post-Strengthening Wetting/drying Cycles

Effects of Reinforcement Corrosion and Sustained Load on Mechanical Behavior of Reinforced Concrete Columns.

Stiffness Degradation for Fatigue of Reinforced Concrete Beams after Electrochemical Rehabilitation

Static and Fatigue Behavior of Steel-Concrete Composite Beams with Corroded Studs

Simplified Methodology for the Evaluation of the Residual Strength of Corroded Reinforced Concrete Beams

Experimental and theoretical study on the mechanical behavior of concrete confined by corroded stirrups