Abstract:This paper reports the synthesis of semiconductor nanocrystals of PbS through a facile and inexpensive synthetic route between lead acetate [Pb(Ac)2·3H2O] and dithioglycol (HSCH2CH2SH) without any surfactant. The products were characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), Raman spectroscopy, x-ray photelectron spectroscopy (XPS) and infrared (IR) spectroscopy. The size of cube-shaped PbS nanocrystals can be controlled by changing the relative amount of Pb(Ac)2·3H2O and dithioglycol. Smaller cube-shaped PbS nanocrystals were obtained at higher sulfur content in the reaction system. The nanometre-sized single crystals of PbS measure ~83 nm × 59 nm × 22 nm and 39 nm × 10 nm × 7 nm, for lead acetate:dithioglycol ratios of 1:0.375 (denoted as PbS-1) and 1:1.5 (denoted as PbS-2), respectively, when a mixture of NaOH solution of lead acetate and ethyl alcohol solution of dithioglycol is maintained at 220 °C for 4 h in a Teflon-lined autoclave. XRD patterns and HRTEM images confirm the crystalline structure of the PbS crystals. TEM helped to determine the dimension of the single crystals. Raman, XPS and IR helped to further demonstrate the purity of the as-synthesized samples. The optical absorption spectra of suspensions of the these crystals in glycol show shifts in absorption band edge for as-prepared sample PbS-1 from 246 to 271 nm and for PbS-2 from 246 to 275 nm, after four days of storage, respectively. The photoluminescence peaks from the two samples are located at 434 and 433 nm for photoexcitation radiation of 315–355 nm, thus exhibiting a Stokes shift compared with band edge energy. The principal contribution of this work is that the nanometre-size PbS single crystals are prepared without using a surfactant or templating agent. The formation of a five-membered ring via the chelation between the Pb2+ ion and dithioglycol is considered to be crucial in this mechanism.

One-step synthesis and optical properties of PbS quantum dots

One-pot aqueous synthesis of near infrared emitting PbS quantum dots

Top-Down Synthesis of N-Type PbS Quantum Dots with High Photoluminescence Quantum Yield from Microsized Pb(OH)Cl

FACILE SYNTHESIS OF COLLOIDAL PbS QUANTUM DOTS

One-pot, easy and scalable synthesis of large-size short wave length IR emitting PbS quantum dots

A Top–down Strategy Towards Monodisperse Colloidal Lead Sulphide Quantum Dots

Controlled Synthesis Of Near-Infrared Quantum Dots For Optoelectronic Devices

Aqueous Synthesis of CdTe/CdS/ZnS Quantum Dots and Their Optical and Chemical Properties

One-step and rapid synthesis of composition-tunable and water-soluble ZnCdS quantum dots

Growth and photoluminescence properties of PbS nanocubes

In situ passivation for high-quality PbS colloidal quantum dots synthesized using a PbBr2 precursor

Quantum Dots: Single Halide Perovskite/Semiconductor Core/Shell Quantum Dots with Ultrastability and Nonblinking Properties (adv. Sci. 18/2019)

Ultrasound-assisted synthesis of PbS quantum dots stabilized by 1,2-benzenedimethanethiol and attachment to single-walled carbon nanotubes

Room-Temperature, Multigram-Scale Synthesis and Conversion Mechanism of Highly Luminescent Lead Sulfide Quantum Dots

A facile synthesis route for preparing aqueous colloidal CdS quantum dots with size-tunable optical properties

Pioneering method for the synthesis of lead sulfide (PbS) nanoparticles using a surfactant-free microemulsion scheme

A facile method for the synthesis of CuInS2–ZnS quantum dots with tunable photoluminescent properties

Stable Monodisperse Pb<sub>1-<i>x</i></sub>Cd<sub><i>x</i></sub>S Quantum Dots for NIR-II Bioimaging by Aqueous Coprecipitation of Bimetallic Clusters

Synthesis of Near Infrared Pbs Quantum Dots by Pyrolysis of Organometallic Sulfur Complex

Continuous flow synthesis of PbS/CdS quantum dots using substituted thioureas

Size tunable and controllable synthesis of PbS quantum dots for broadband photoelectric response