Abstract:Zeolite Y films (0.35-2.5 μm), into which CdS and PbS quantum dots (QDs) were loaded, were grown on ITO glass. The CdS QD-loaded zeolite Y films showed a photovoltaic effect in the electrolyte solution consisting of Na(2)S (1 M) and NaOH (0.1 M) with Pt-coated F-doped tin oxide glass as the counter electrode. In contrast, the PbS QD-loaded zeolite Y films exhibited a negligible PV effect. This contrasting behavior was proposed to arise from the large difference in driving force for the electron transfer from S(2-) in the solution to the hole in the valence band of QDs, with the former being much larger (~2 eV) than the latter (~1 eV). In the case of CdS QD-loaded zeolite Y with a loaded amount of CdS of 6.3 per unit cell, the short circuit current, open circuit voltage, fill factor, and efficiency were 0.3 mA cm(-2), 423 V, 28, and 0.1%, respectively, under the AM 1.5, 100 mW cm(-2) condition. This cell was stable for more than 18 days of continuous measurements. A large (3-fold) increase in overall efficiency was observed when PbS QD-loaded zeolite Y on ITO glass was used as the counter electrode. This phenomenon suggests that the uphill electron transfer from ITO glass to S in the solution is facilitated by the photoassisted pumping of the potential energy of the electron in ITO glass to the level that is higher than the reduction potential of S by PbS QDs. Under this condition, the incident-photon-to-current conversion efficiency (IPCE) value at 398 nm was 42% and the absorbed-photon-to-current conversion efficiency (APCE) value at 405 nm was 82%. The electrolyte-mediated interdot charge transport within zeolite films is concluded to be responsible for the overall current flow.

Photocatalysis Of Pbs Quantum Dots In A Quantum Dot-Sensitized Solar Cell: Photovoltaic Performance And Characteristics

Synthesis and Characterization of Bi2S3 Quantum Dot-Sensitized TiO2 Nanorod Arrays Coated with ZnSe Passivation Layers

Construction of TiO2 NP@TiO2 NT Double-Layered Structural Photoanode to Enhance Photovoltaic Performance of CdSe/CdS Quantum Dots Sensitized Solar Cells

Octahedron Shaped Lead Sulfide Nanocrystals As Counter Electrodes for Quantum Dot Sensitized Solar Cells

Study on silicon quantum dots sensitized solar cells

TiO2 surface modification and characterization with nanosized PbS in dye-sensitized solar cells.

Structure and Morphology of Quantum Dots Modifying Tio<Subscript>2</Subscript> Nanoporous Film in Dye-Sensitized Solar Cells

Fabrication and Photoelectrochemical Performance of CdS Quantum Dots Sensitized TiO2 Film Electrodes

In Situ Passivation for Efficient PbS Quantum Dot Solar Cells by Precursor Engineering

Synthesis of Size-Adjustable CsPbBr3 Perovskite Quantum Dots for Potential Photoelectric Catalysis Applications

In situ passivation for high-quality PbS colloidal quantum dots synthesized using a PbBr2 precursor

PbSe Quantum Dot Solar Cells Based on Directly Synthesized Semiconductive Inks

Novel PbS Quantum Dots Sensitized Flower-Like BiOBr with Enhanced Photocatalytic Properties under Visible Light

The Effect of Photoanode Structure on the Performances of Quantum-Dot-Sensitized Solar Cells: A Case Study of the Anatase Tio2 Nanocrystals and Polydisperse Mesoporous Spheres Hybrid Photoanodes

Facile Sonication Synthesis of WS2 Quantum Dots for Photoelectrochemical Performance

Photocatalytic Formation of P–S Bonds Via CdSeS/CdZnS Quantum Dots under Visible Light Irradiation

FACILE SYNTHESIS OF COLLOIDAL PbS QUANTUM DOTS

Optimizing Surface Passivation of n‐Type Quantum Dots for Efficient PbS Quantum Dot Solar Cells

Structure and Morphology of Nanosized Pbs on Tio2 Nanoporous Film in Dye-Sensitized Solar Cells

Photovoltaic effects of CdS and PbS quantum dots encapsulated in zeolite Y

Electron Injection and Photovoltaic Properties in Cdse/Zns Quantum Dot Sensitized Solar Cells