Abstract:The crystallization process of β zeolite has been investigated by using FT-IR, XRD, TG, SEM, and ICP-AES. The samples were obtained by hydrothermal synthesis at 140 °C and chemical composition of the mixture used for synthesis can be expressed as n(Al2O3) : n(SiO2) : n(TEABr) : n (Na2O) : n(NaF) : n(H2O) : n [(NH4)2O] = 1 : 25 : 7. 5 : 2. 5 : 3. 75 : 550 : 6. 25. The crystallization curve of zeolite β exhibits a typical S-shaped characteristic. The typical framework IR-absorptions at 567 and 518 cm-1 have different natures. The former is detected at the beginning of induction period and its intensity changes a little in induction period, but exhibits a direct correlation with crystallinity in growth period. The latter is not detected in the induction period, but exhibits the same trend in growth period. The large amorphous SiO2-Al2O3 particles which are visible at the beginning of crystallization change into small grains during the induction period. n(SiO2)/n(Al2O3) ratio of the solid phases obtained at different synthesis time changes significantly during the induction period, but changes a little in growth period. So the β zeolite crystal nucleus are formed via liquid-phase synthesis mechanism. A typical gel in synthesis of β zeolite is transformed initially into a solid, which contains richer aluminium, minor F- and occluded TEA species. The aluminosilicate gel particles are dissolved by F- during the induction period and the transition complex, which has a specific weak X-ray diffraction peak at 2θ = 22. 8° and specific DTG pattern, is formed at the turning point from induction period to growth period. During the growth period Si and Al transport from the liquid to the solid phase at almost the same rates. F- anion has greater influence on the formation and turning of transition complex.

Synthesis Of Boron-Containing Cf-2 Zeofite By Self-Transformation Of Porous Glass Granules In A Vapor Phase

Preparation and Characterization of B-containing Zeolite CF-2 by Self-transformation of Porous Glass Granules in a Vapor Phase

Preparation of Boron-Containing Ton-Type Zeolite by Self-Transformation of Porous Glass in A Vapor Phase

State changes of methylamine molecules in synthetic process of boron-containing CF-2 zeolite by solid-phase transformation

Synthesis and Structural Characterization of B-Al-ZSM-5 Zeolite from Boron–silicon Porous Glass in the Vapor Phase

Studies on zeolite synthesis by self-transformation of B-containing porous glass in a vapor phase: I. Solid-state surface reaction

The synthesis and characterization of zeolite ZSM-5 and ZSM-35 films by self-transformation of glass

Synthesis of zeolite Li-ABW from fly ash by fusion method

Preparation of an MFI-type zeolite membrane on a porous glass disc by substrate self-transformation

Solvent-Free Secondary Growth of Highly B-Oriented MFI Zeolite Films from Anhydrous Synthetic Powder.

Fabrication of B‐oriented MFI Zeolite Films under Neutral Conditions Without the Use of Hydrogen Fluoride

Rapid fabrication of highly b-oriented zeolite MFI thin films using ammonium salts as crystallization-mediating agents

Synthesis of b-Oriented MFI-Type Zeolite Membrane on Porous Glass Support by in Situ Hydrothermal Crystallization

Synthesis zeolites in water vapour phase and their properties

Controlled Release of Siliceous Species for the Fabrication of Highly B-Oriented MFI Zeolite Films

Synthesis of β Zeolite Using Tetraethylammonium Bromide Together with Fluoride as Composite of Template (II) - Studies on Crystallization Process of β Zeolite

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

Synthesis of Millimeter-Sized Spherical Ferrierite Zeolite by Vapor-Assisted Conversion

Use of Borosilicate Seeds to Synthesize Aluminosilicate SSZ-82, a Zeolite Containing Intersecting 12- and 10-Membered Ring Channels

Synthesis of all-silica zeolite beta

High-Silica Ferrierite Zeolite Self-Transformed From Aluminosilicate Gel