Abstract:Mordenite and ZSM-5 seeds could grow on the surface of an asymmetric α-Al2O3 support using an identical organic-free aluminosilicate solution under the same hydrothermal conditions. It suggests that the phase of zeolite can be controlled by varying the type of seed. Continuous mordenite and ZSM-5 membranes were prepared by the secondary growth method using corresponding seeds under appropriate conditions. The water content in the secondary growth mixture strongly influenced the growth of zeolite crystals. ZSM-5 seeds grew at a smaller rate and showed a habit of thin hexagonal plate in a concentrated mixture, while the crystals with a habit of rectangular parallelepiped were formed from a diluted secondary growth mixture. ZSM-5 crystals had poor intergrowth in the former case, whereas the crystals were highly intergrown in the latter case. ZSM-5 crystals in either membrane have a random orientation. In contrast to ZSM-5 zeolite, the crystal orientation in the secondary grown mordenite membranes strongly depended on the water content in the secondary growth mixture. The crystals in the mordenite membrane developed in a diluted secondary growth mixture were oriented with the (150) face parallel to the support surface, whereas the crystals in the membrane grown in a concentrated mixture were oriented with the (002) face parallel to the support surface. These results suggest that the crystal orientation in mordenite membranes can be manipulated only by changing the water content in a secondary growth mixture. The formation of the preferred crystal orientation in the secondary grown mordenite membrane is discussed in terms of an “evolutionary selection” process.

Synthesis of b-Oriented MFI-Type Zeolite Membrane on Porous Glass Support by in Situ Hydrothermal Crystallization

The control of phase and orientation in zeolite membranes by the secondary growth method

A Facile Fabrication of Highly B-Oriented Mfi Zeolite Films in the Teos-Tpaoh-H2o System Without Additives

Fabrication of B-Oriented MFI Zeolite Membranes by a Printing-Transfer Seed Layer Procedure.

Fabrication of B‐oriented MFI Zeolite Films under Neutral Conditions Without the Use of Hydrogen Fluoride

Insights into 1,2-Dihydroxybenzene Addition on Twin Suppression During the Secondary Hydrothermal Synthesis of B-Oriented MFI Zeolite Films

Controlling Crystal Orientation in Zeolite MFI Thin Films by Direct In Situ Crystallization

Induction of Zeolite Membrane Formation by Implanting Zeolite Crystals into the Precursor of Ceramic Supports

Oriented Zeolite Mfi Monolayer Films on Metal Substrates by in Situ Crystallization

Effects of the synthesis hydrogel on the formation of zeolite LTA membranes

Gel-less Steam-Assisted Crystallization of Platelike MFI Crystals for the Fabrication of B-Oriented Zeolite Membranes

Ultrasonic-assisted Fabrication of High Flux T-type Zeolite Membranes on Alumina Hollow Fibers

Preparation and permeability performances of MFI zeolite membranes by in-situ crystallization method

Microstructure Manipulation of MFI-type Zeolite Membranes on Hollow Fibers for Ethanol–water Separation

Dynamic Hydrothermal Synthesis of a B-Oriented MFI Zeolite Film

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

Synthesis of highly b-oriented zeolite MFI films by suppressing twin crystal growth during the secondary growth

Preparation of an MFI-type zeolite membrane on a porous glass disc by substrate self-transformation

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Solvent-Free Secondary Growth of Highly B-Oriented MFI Zeolite Films from Anhydrous Synthetic Powder.

Preparation of high-performance zeolite membrane on a macroporous support by novel intermittent hydrothermal synthesis