Abstract:Mordenite and ZSM-5 seeds could grow on the surface of an asymmetric α-Al2O3 support using an identical organic-free aluminosilicate solution under the same hydrothermal conditions. It suggests that the phase of zeolite can be controlled by varying the type of seed. Continuous mordenite and ZSM-5 membranes were prepared by the secondary growth method using corresponding seeds under appropriate conditions. The water content in the secondary growth mixture strongly influenced the growth of zeolite crystals. ZSM-5 seeds grew at a smaller rate and showed a habit of thin hexagonal plate in a concentrated mixture, while the crystals with a habit of rectangular parallelepiped were formed from a diluted secondary growth mixture. ZSM-5 crystals had poor intergrowth in the former case, whereas the crystals were highly intergrown in the latter case. ZSM-5 crystals in either membrane have a random orientation. In contrast to ZSM-5 zeolite, the crystal orientation in the secondary grown mordenite membranes strongly depended on the water content in the secondary growth mixture. The crystals in the mordenite membrane developed in a diluted secondary growth mixture were oriented with the (150) face parallel to the support surface, whereas the crystals in the membrane grown in a concentrated mixture were oriented with the (002) face parallel to the support surface. These results suggest that the crystal orientation in mordenite membranes can be manipulated only by changing the water content in a secondary growth mixture. The formation of the preferred crystal orientation in the secondary grown mordenite membrane is discussed in terms of an “evolutionary selection” process.

A Facile Fabrication of Highly B-Oriented Mfi Zeolite Films in the Teos-Tpaoh-H2o System Without Additives

Fabrication of B‐oriented MFI Zeolite Films under Neutral Conditions Without the Use of Hydrogen Fluoride

Synthesis of highly b-oriented zeolite MFI films by suppressing twin crystal growth during the secondary growth

Solvent-Free Secondary Growth of Highly B-Oriented MFI Zeolite Films from Anhydrous Synthetic Powder.

Insights into 1,2-Dihydroxybenzene Addition on Twin Suppression During the Secondary Hydrothermal Synthesis of B-Oriented MFI Zeolite Films

Enhanced Compactness of Oriented MFI Zeolite Films by Heat Treatment of Seed Layer

Controlled Release of Siliceous Species for the Fabrication of Highly B-Oriented MFI Zeolite Films

Rapid fabrication of highly b-oriented zeolite MFI thin films using ammonium salts as crystallization-mediating agents

Oriented Zeolite Mfi Monolayer Films on Metal Substrates by in Situ Crystallization

High-Light-Transmittance and Low-Haze Antifog MFI Zeolite Films Fabricated by Solvothermal Secondary Growth

Controlling Crystal Orientation in Zeolite MFI Thin Films by Direct In Situ Crystallization

The control of phase and orientation in zeolite membranes by the secondary growth method

Fabrication of B-Oriented MFI Zeolite Membranes by a Printing-Transfer Seed Layer Procedure.

Dynamic Hydrothermal Synthesis of a B-Oriented MFI Zeolite Film

Thermal processing of zeolite seed layers for the fabrication of compact oriented MFI zeolite films

Synthesis of b-Oriented MFI-Type Zeolite Membrane on Porous Glass Support by in Situ Hydrothermal Crystallization

Oriented Films of Epitaxial Mfi Overgrowths

Microstructural Manipulation of MFI-type Zeolite Films/membranes: Current Status and Perspectives

Oriented MFI films for gas phase separation, catalysis, and sensing: A review of crystal growth, design, and function enabling

Calcination-Free Fabrication of Highly B-Oriented Silicalite-1 Zeolite Films by Secondary Growth in the Absence of Organic StructureDirecting Agents

Twin Suppression Effect of Dihydroxy-Benzene Isomers During the Secondary Growth of B-Oriented Zeolite MFI Nanosheet Films