Abstract:Mordenite composite membranes were prepared by means of coating a porous α-alumina support with nanosized mordenite seeds followed by hydrothermal crystallization. A systematic investigation was performed on the influence of several factors such as ageing of the reaction mixture, alkalinity, salt addition and temperature on the formation of a mordenite membrane on the seeded support. The ageing of the reaction mixture reduces the growth rate of mordenite crystal along a-axis and b-axis but hardly influences the growth rate along c-axis. As a result, the boundaries between the surface crystals become a little larger with prolonging the period of ageing time. The growth rate of the mordenite crystal along individual axes increases first and then decreases with increasing concentration of sodium hydroxide. A higher alkalinity is unfavorable for the formation of a continuous mordenite membrane. The addition of salt in the reaction mixture has different effect on the growth rate of the mordenite crystal along each axis. With increasing the amount of salt, there was hardly influence on the growth rate along c-axis, whereas an obvious decline was observed in the growth rate along either a-axis or b-axis, which enlarges the boundaries between the surface crystals. The growth rate of the mordenite crystal increases more along c-axis than that along a-axis or b-axis with increasing temperature for hydrothermal crystallization. The use of a temperature as high as 473 K produces a membrane composed of bar-like crystals with larger boundaries.

Preparation of an MFI-type zeolite membrane on a porous glass disc by substrate self-transformation

Synthesis of b-Oriented MFI-Type Zeolite Membrane on Porous Glass Support by in Situ Hydrothermal Crystallization

Fabrication of B-Oriented MFI Zeolite Membranes by a Printing-Transfer Seed Layer Procedure.

Growth Mechanism of a Preferentially Oriented Mordenite Membrane

Effects of porogen EDTA on morphology of porous silica support and preparation of MFI zeolite membrane

High-Light-Transmittance and Low-Haze Antifog MFI Zeolite Films Fabricated by Solvothermal Secondary Growth

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Microstructure Manipulation of MFI-type Zeolite Membranes on Hollow Fibers for Ethanol–water Separation

Preparation of Mordenite Composite Membranes with Seeding

Preparation of Ferrierite Zeolite Membranes in the Absence of Organic Structure-directing Agents

Preparation and characterization of preferentially oriented continuous MFI-type zeolite membranes from porous glass

Preparation of zeolite MFI membranes on defective macroporous alumina supports by a novel wetting–rubbing seeding method: Role of wetting agent

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

Fabrication of Zeolite Naa Membranes on Hollow Fibers Using Nano-Sized Seeds Exfoliated from Mesoporous Zeolite Crystals

Preparation of Boron-Containing Ton-Type Zeolite by Self-Transformation of Porous Glass in A Vapor Phase

Induction of Zeolite Membrane Formation by Implanting Zeolite Crystals into the Precursor of Ceramic Supports

Fabrication of B‐oriented MFI Zeolite Films under Neutral Conditions Without the Use of Hydrogen Fluoride

Zeolite Mfi Membranes for Separation of Ethanol/Water Mixture

Preparation of Asymmetric Zeolite NaA Membrane Layers by Vapor Phase Transfer and Seeded Growth Method

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.