Passivity of Martensitic Stainless Steel in Borate Buffer Solution: Influence of Sulfide Ion
Xiaowei Lei,Hongyan Wang,Nan Wang,Dazhong Ren,Anqing Fu,Chengxian Yin,Junping Zhang,Yaorong Feng,Digby D. Macdonald
DOI: https://doi.org/10.1016/j.apsusc.2019.01.250
2019-01-01
Applications of Surface Science
Abstract:Upon performing electrochemical measurements, XPS and TEM characterizations, the influence of sulfide on the passive behavior of Super 13Cr martensitic stainless steel was deciphered. Mechanism interpretation is performed by optimizing the Point Defect Model based upon the impedance data. It is revealed that the passive film display n-type semiconductivity, and the donor density dropped with increasing concentration of sulfide ion. Sulfide ion can induce a current peak at −250 mVSCE (Epeak). The addition of Na2S generates a continuous outer layer which is comprised of Cr(OH)3, FeS2 and FeS at potential lower than Epeak, and Cr(OH)3 at potential higher than Epeak. This result leads to the thinner barrier layer and lower charge transfer resistance, implying a weaker protection of the substrate by the passive film.