Abstract:The quality of concrete surfaces is negatively affected by the plateau climate. The purpose of present study was to investigate the mechanism of the climate effect on the microstructures and properties of concrete surfaces under different exposure conditions. Scanning electron micro-scopy, X-ray diffraction, thermogravimetry, nitrogen adsorption porosimetry, mercury intrusion porosimetry, and microhardness tests were used for microstructure analysis. Rebound strength and abrasion resistance tests were conducted to assess the mechanical properties. Tests of sorp-tivity under various absorption conditions, chloride ion impenetrability after vacuum saturation and immersion, and deicing salt scaling with natural and standard freeze-thaw cycling, were conducted to assess the durability. The results showed that both cement hydration and micro-structure densification of the exposed concrete surfaces were lower than those of the concrete interior, leading to worse mechanical properties and durability. The rapid moisture loss, rather than the low temperature, was the dominant cause of the weak surface layer, with a depth be-tween 10 mm and 15 mm. The performance of a south-oriented surface was slightly better than that of a north-oriented surface, which was due to the stronger solar radiation for the former surface. However, the difference was so small that it could be ignored. Furthermore, the concrete sorptivity under the conditions of semi-immersion and vacuum saturation was lower in the high-altitude regions, which was due to the higher evaporation and smaller pressure difference after vacuum absorption. Thus, significant errors were expected in all tests of chloride ion impene-trability assessment conducted in high-altitude regions.

Effect of Low Atmospheric Pressure on Air Entrainment in Cement-Based Materials: an On-Site Experimental Study at Different Elevations

Rheology and air entrainment of fresh Portland cement mortars in simulated low air pressure environments

Effects of Atmospheric Pressure on Developmental Characteristics and the Stability of Air Entraining Agent for Concrete

Effect of low air pressure on the durability of concrete

Investigation on air-voids structure and compressive strength of concrete at low atmospheric pressure

Simulation Analysis of Pumping Characteristics for High-Altitude Concrete

Early-age Shrinkage Behavior of Cement-Fly Ash Paste under Wind Speeds: A Study Using BSE-IA and MIP Techniques

Characteristic Analysis of Concrete Air Entraining Agents in Different Media

Effect of the entrained air void on strength and interfacial transition zone of air-entrained mortar

Experimental investigation on fractal characteristics of pores in air-entrained concrete at low atmospheric pressure

Effect of nanomaterials on the mechanical properties and microstructure of cement mortar under low air pressure curing

Physical Properties and Hydration Characteristics of Low-Heat Portland Cement at High-Altitude

Both Plasticizing and Air-Entraining Effect on Cement-Based Material Porosity and Durability

Experimental Investigation on the Effect of High-Pressure Water on Tensile Strength and Microstructure of Cementitious Materials

Effect of Salt Admixtures on Air Content in Fresh Air-Entrained Concretes

Microstructures and Properties of Concrete Surfaces under Different Exposure Conditions in Complex Natural Environments of High-Altitude Regions

Microstructural changes of young cement paste due to moisture transfer at low air pressures

Development of Pore Pressure in Cementitious Materials under Low Thermal Effects: Evidence from Optimization of Pore Structure by Incorporation of Fly Ash

Influences of Air-Voids on the Performance of 3D Printing Cementitious Materials

Effect of Sodium Sulfate and Sodium Nitrite on Air-Void System in Air-Entrained Concrete

Influence of Early Hydration Process on the Hydrostatic Pressure Change of Cement Pastes at Different Temperatures