Abstract:A fast cooling freeze casting (FCFC) method was developed for preparation of porous Al2O3 scaffolds with improved interconnectivity, unidirectional pore channels and dendritic walls. As estimated using the Archimedes method and mercury porosimetry, total porosity 64.5–68.5vol% and the closed porosity <0.6vol% reveal that most pores are open. The bimodal pore size distribution shifted to larger diameters with increasing sodium-hexametaphosphate (SHMP) concentration from 0.1% to 0.5%. Scanning electronic microscope (SEM) images of the resultant porous Al2O3 showed clear transformation from lamellae to dendrite structures with increasing polyvinyl alcohol (PVA) concentration from 1% to 3%. To discover the mechanism, the freezing curve of the Al2O3 slip was achieved, showing its supercooling point at about −10°C where most isolated water solidifies at an average ice front velocity of 0.42μm/s. Together with the PVA effects on the microstructure transformation, the underlying mechanism could be ascribed to both the supercooling and PVA effects. The lamellae ice front was initially formed under this velocity, but with increasing PVA, the ceramic slurry got more viscous and the rearrangement of ceramic particles was hindered, hence the ice front growth in the preferred a direction was limited whereas the growth in the c direction was promoted. Meanwhile under the effects of the applied thermal gradient, the lamellae were transformed into dendrite structures.

Alumina Aerogels with Unidirectional Channels under Different Freezing Temperatures During Freeze Casting—part I: Control and Analysis of Pore Channels

Alumina aerogels with unidirectional channels under different freezing temperatures during freeze casting——Part II: Anisotropic mechanical and thermal conductive properties

Synthesis and Anisotropic Properties of Alumina-Silica Aerogels Constructed by Silica Sols Infiltrated into Unidirectional Frozen Alumina Templates

Preparation of Alumina Aerogel via Supercritical Method

Ice-Templating of Alumina Suspensions: Effect of Supercooling and Crystal Growth During the Initial Freezing Regime

On Controlling Aerogel Microstructure by Freeze Casting

Preparation and characterization of monolithic alumina aerogels

Influence of fibers on the microstructure and compressive response of directional ice-templated alumina ceramics

Synthesis of Alumina Aerogels by Ambient Drying Method and Control of Their Structures

The controllable microstructure of porous Al2O3 ceramics prepared via a novel freeze casting route

Hydrothermal assisted synthesis of heat resistant, well-crystallized aerogels constructed by boehmite nano rods

Effect of particle size on the lamellar pore microstructure of porous Al2O3 ceramics fabricated by the unidirectional freezing

Freeze gelcasting of aqueous alumina suspensions for porous ceramics

Freeze-Casting of Alumina and Permeability Analysis Based on a 3D Microstructure Reconstructed Using Generative Adversarial Networks

Ice-templated porous alumina structures

Porous Alumina Ceramics Produced by Physical Vapor Deposition Assisted Freeze-Casting Method

Fully interconnected porous Al 2 O 3 scaffolds prepared by a fast cooling freeze casting method

Preparation and Thermal Stablity of Silica- alumina-fibers Composite Aerogels

Alumina Porous Ceramics Obtained by Freeze Casting: Structure and Mechanical Behaviour under Compression

Microstructure Evolution During the Sintering of Freeze-Cast Alumina

Control of pore channel size during freeze casting of porous YSZ ceramics with unidirectionally aligned channels using different freezing temperatures