Effect of particle size on the lamellar pore microstructure of porous Al2O3 ceramics fabricated by the unidirectional freezing

Xiaoyong Zhang,Yan Zhang,Dou Zhang

DOI: https://doi.org/10.4028/www.scientific.net/AMM.184-185.818

2012-01-01

Applied Mechanics and Materials

Abstract:Porous Al2O3 ceramics with a lamellar pore microstructure have been fabricated by a directional freezing process using the micro-sized and nano-sized Al2O3 powders. At the same solid loading and freezing temperature, compared with the suspensions of micro-sized Al2O3, the porous ceramics prepared from the suspensions of nano-sized Al2O3 had the narrower lamellar pore channels and thicker channel walls, which were caused by the higher viscosity, stronger inter-particle attraction and more ice nucleation sites in the nano-sized Al2O3 suspensions. For both types of Al2O3 at a specific solid loading, with the increasing of freezing temperature, the wider pore channels and thinner channel walls were observed. These tendencies were weaker by using the nano-sized Al2O3. The above results show the lower porosity in the ceramics using the nano-sized Al2O3. However, due to the higher sintering activity for the smaller particles, the pore channel walls by using the nano-sized Al2O3 was denser than using the micro-sized Al2O3, leading to the higher mechanical strength of ceramics.