Fatigue response of Nafion® XL membrane in biaxial tension: Temperature effects

Lei Su,Qing An,Jiejie Li,Lin Wang,Yuhang Zhang,Hongjian Zhou,Re Xia

DOI: https://doi.org/10.1111/ffe.13465

2021-04-04

Abstract:Fatigue & Fracture of Engineering Materials & Structures, EarlyView.

materials science, multidisciplinary,engineering, mechanical

What problem does this paper attempt to address?

Temperature-dependent fatigue crack growth mechanisms of fuel cell membranes

Shouwen Shi,Jiayao Li,Haiyan Li,Yihao Yao,Hailong Dai,Yuanjie Fu,Qiang Lin,Xu Chen

DOI: https://doi.org/10.1016/j.ijfatigue.2021.106554

IF: 5.489

2022-01-01

International Journal of Fatigue

Abstract:The fatigue crack growth behaviors of two fuel membranes are investigated at different temperatures. Fatigue crack growth rate increases with temperature, and Nafion XL membrane is more sensitive to temperature. An Arrhenius-type expression for fatigue crack growth rate is proposed and good prediction results are obtained. For Nafion XL composite membrane, fatigue crack grows by forming micropores ahead of crack tip. These micropore are formed due to the combined action of hygrothermal environment and mechanical stress, which increase with temperature. Besides, the interior micropores and microstructure changes in reinforcement layer also account for higher temperature sensitivity of Nafion XL membrane.

materials science, multidisciplinary,engineering, mechanical
Effects of Microstructure on the Retention of Proton Conductivity of Nafion/SiO2 Composite Membranes at Elevated Temperatures:An in Situ SAXS Study

Jianchun Niu,Shuomeng Zhang,Yunqi Li,Xiaoyu Li,Jialin Zhang,Shanfu Lu,Qinggang He

DOI: https://doi.org/10.1016/j.polymer.2023.125869

IF: 4.6

2023-01-01

Polymer

Abstract:The operating temperature of modified Nafion membranes remains too low to satisfy the requirements for hightemperature proton exchange membrane fuel cells (HT-PEMFCs) because most can only operate well below 120 degrees C. In this article, we prepare a series of Nafion/SiO2 composite membranes with different contents of doped silica nanoparticles by in situ growth of SiO2 nanoparticles near the -SO3H group. The water dynamic change process and the functional properties of Nafion/SiO2 composite membranes are studied and found to correlate well with structural parameters, such as crystallinity and average chain spacing. Also, microstructure information including the phase separation structure changes, structural complexity, and ion cluster fraction of Nafion/ SiO2 composite membranes at different temperatures are investigated using synchrotron-based in situ small angle X-ray scattering (SAXS). Differing from expectations, the amount of water in the Nafion/SiO2 composite membranes may not be the decisive factor to maintain proton conductivity at relatively high temperatures. Instead, the complexity or connectivity of the proton transport channel may play a more important role in the effective proton transfer inside the composite membranes, which also provides valuable guidance and insight for the development of novel HT-PEM materials with well-designed ion transport pathways in the future.
Temperature‐dependent mechanical performance of Nafion® 212 proton exchange membrane under uniaxial and biaxial loading

Yiqun Hu,Suhang Ding,Mingxing Pan,Jianfei Xu,Yuhang Zhang,Wenwang Wu,Re Xia

DOI: https://doi.org/10.1002/app.54271

IF: 3

2023-06-13

Journal of Applied Polymer Science

Abstract:Biaxial tensile fatigue test of Nafion® 212 proton exchange membrane. The degradation of proton exchange membranes (PEMs) can significantly affect the structural integrity and lifetime of fuel cells. This study investigates the effects of temperature, peak load, initial strain, and loading modes on the mechanical properties of Nafion® 212 PEM using an in‐situ biaxial testing system. The findings indicate that membrane creeping is positively correlated with temperature and peak loads. The stress relaxation rate increases with the increase of initial strain, and an increase in temperature also leads to an apparent decrease in the anti‐relaxation properties of Nafion® 212 membrane. Additionally, the mechanical properties of low‐cycle fatigue at various temperatures were explored under biaxial cyclic loading conditions. When the temperature is fixed, the membrane strain increases and gradually stabilizes with the rise of fatigue cycles. With an increase in temperature, the strain increases at a greater rate. The phase difference increases with temperature growth, and the "hysteresis" phenomenon of the strain becomes more pronounced, resulting in greater energy loss. These results provide valuable insights into the mechanical behavior of Nafion® 212 PEM under different conditions. And can inform the design and optimization of fuel cell systems and contribute to the development of more robust and durable PEM materials.

polymer science
Continuum Approach for Modeling Mechanical Fatigue of Ionomer Membrane

Wenqing Liu,Diankai Qiu,Linfa Peng,Xinmin Lai

DOI: https://doi.org/10.1149/ma2020-02352254mtgabs

2020-01-01

ECS Meeting Abstracts

Abstract:The mechanical degradation of the proton exchange membrane is one of the main aspects affecting the lifetime of proton exchange membrane fuel cell. In previous study, we have found a plastic deformation occurs after the temperature and water content are increased, and would be substantially enhanced by the gas pressure difference between the anode and cathode. We further concentrates on the stress/strain evolution in the membrane of fuel cells throughout the assembly and running processes. However, the polymer electrolyte membranes suffers complex hygrothermal loading in the running process and show unlinear visco-elastic–plastic behavior. Thus the membrane express a different fatigue behavior compared to traditional metal materials. We propose an approach suitable for modeling mechanical degradation in polymer electrolyte membranes based on a constitutive model of Nafion membrane considering the rate, temperature, and hydration dependent deformation response under cyclic loading. A finite element analysis was performed and the results were compared to experimental observations.
Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Duyi Ye,Yuandong Xu,Lei Xiao,Haibo Cha

DOI: https://doi.org/10.1016/j.msea.2010.03.027

2010-01-01

Abstract:A series of experiments, including constant amplitude low-cycle fatigue tests, post-fatigue tension to failure tests, LOM (TEM) observations, and SEM examinations, were performed at room-temperature to investigate the effects of low-cycle fatigue damage on the static mechanical properties, microstructures and fracture behavior of 304 austenitic stainless steel. The changing characteristics of various static mechanical property parameters, including the strength parameters (σys and σult), stiffness parameter (E), ductility parameters (δ and φf) and strain hardening exponent (n) during fatigue damage process of the stainless steel were obtained experimentally and their micromechanisms were discussed by analyzing both the deformation microstructures and the fracture features of cyclically pre-deformed specimens. It was shown that the austenite/martensite transformation resulting from the accumulation of cyclic plastic strain was mostly responsible for the variation in the strength, ductility and strain hardening ability of the stainless steel during fatigue damage process. The depletion of the inherent ductility in the material due to fatigue damage evolution led to the ductile-to-brittle transition (DBT) in the fracture modes. Based on the macro/micro-experiments regarding the exhaustion of the ductility during fatigue damage, the ductility parameter was suggested as a damage indicating parameter for the present stainless steel in further studying the fatigue damage mechanics model as well as the residual fatigue life prediction method.
Fatigue crack propagation behavior of fuel cell membranes after chemical degradation

Shouwen Shi,Xiaoyi Sun,Qiang Lin,Jian Chen,Yuanjie Fu,Xiaodong Hong,Cong Li,Xiang Guo,Gang Chen,Xu Chen

DOI: https://doi.org/10.1016/j.ijhydene.2020.07.113

IF: 7.2

2020-10-01

International Journal of Hydrogen Energy

Abstract:The durability of fuel cells is significantly impaired by chemical and mechanical degradations of perfluorosulfonic-acid membranes. However, how the mechanical degradation, especially the fatigue crack propagation behavior, is impacted by chemical degradation is not clear. In this paper, the fatigue crack propagation behavior of Nafion 212 and Nafion XL composite membranes after chemical degradation are investigated. The fluoride release rates of Nafion 212 and Nafion XL membrane are 0.335 and 0.095 μmol cm−2 h−1, respectively. Likewise, the fatigue crack propagation rate of Nafion 212 membrane is also larger, which is attributed to two fatigue crack propagation mechanisms induced by chemical degradation, including bubble collapsing and pore interconnecting. By contrast, the fatigue crack propagation mechanism of Nafion XL membrane is not significantly changed where chemical degradation only accelerates crack growth in exterior surface layers. These findings provide new insights into the failure mechanisms under combined chemical and mechanical degradations.

energy & fuels,electrochemistry,chemistry, physical
Impact of Initial Cyclic Loading on Mechanical Properties and Performance of Nafion

David Vokoun,Sneha Samal,Ivo Stachiv

DOI: https://doi.org/10.3390/s23031488

IF: 3.9

2023-01-01

Sensors

Abstract:Nafion possesses many interesting properties such as a high ion-conductivity, hydrophilicity, and thermal and chemical stability that make this material highly suitable for many applications including fuel cells and various (bio-)chemical and physical sensors. However, the mechanical properties of a Nafion membrane that are known to be affected by the viscoplastic characteristics of the material itself have a strong impact on the performance of Nafion-based sensors. In this study, the mechanical properties of Nafion under the cyclic loading have been investigated in detail. After cyclic tensile loading (i.e., maximum elongation about 25% at a room temperature and relative humidity about 40%) a time-dependent recovery comes into play. This recovery process is also shown being strain-rate dependent. Our results reveal that the recovery behavior weakens after performing several stress–strain cycles. Present findings can be of a great importance in future design of various chemical and biological microsensors and nanosensors such as hydrogen or glucose ones.
Effect of temperature on dynamic fatigue behaviour of Si3N4 material

Hongjie Wang,Yonglan Wang,Zhihao Jin,Huijiu Zhou

IF: 1.292

1998-01-01

Journal of Inorganic Materials

Abstract:The dynamic fatigue behaviours of Si3N4 material at room temperature, 800 and 1100 degrees C were investigated. It was discovered that the fracture strength decreases with the increase of sigma at a high stress rate, and that the stress corrosion exponent n decreases also with the temperature increasing. The former is the same as that in transformation toughening ceramics and glass-ceramics, but is of some deviation from the theoretical prediction. The fractographic observation showed that the dynamic fatigue failure mechanism of Si3N4 at elevated temperature is the softing of the glass phase in grain boundaries.
Research on the Fatigue Properties of Glass Fiber Composite Laminates

Hai-xia CHEN,Fei LIU,Wen-jun QI,Hua-chao XU

DOI: https://doi.org/10.3969/j.issn.1001-3997.2017.12.014

2017-01-01

Abstract:In order to study the fatigue performance of glass fiber reinforced epoxy resin lamina under high frequency,static tensile experiment and fatigue experiment were carried out at room temperature;the fracture reason and mechanism of glass fiber reinforced epoxy resin lamina are studied by observing the fracture morphology;conducted numerical simulation on the fatigue life of laminated plates by ABAQUS and nCode software,and compared with the test result.The results show that:there are two main zones at the fatigue life curve:high cycle fatigue zone and sub-fatigue zone.The tensile fracture morphology was similar to the fatigue fracture morphology,fiat and orderliness,which presents the typical characteristics of brittle material;fatigue cycles decreased as the mean stress increasing;physical test value is lower than the results of numerical simulation,but the trends are the same,due to the idealization of numerical simulation model and the loading process.The result can provide reference for fatigue life study and engineering test of the composite materials.
Embrittlement Induced Fracture Behavior and Mechanisms of Perfluorosulfonic-Acid Membranes after Chemical Degradation

Xiaoyi Sun,Shouwen Shi,Yuanjie Fu,Jian Chen,Qiang Lin,Jiaqi Hu,Cong Li,Jiayao Li,Xu Chen

DOI: https://doi.org/10.1016/j.jpowsour.2020.227893

IF: 9.2

2020-01-01

Journal of Power Sources

Abstract:Chemical and mechanical degradations of perfluorosulfonic-acid membranes are two factors contributing to the reduced durability of fuel cells. While the mechanisms of isolated chemical or mechanical degradation are extensively investigated, the impact of chemical degradation on mechanical degradation is not fully understood. In this paper, the fracture behavior of Nafion 212 membranes with different chemical degradation levels are investigated. To characterize the degradation level and probe the molecular origins of chemical degradation, fluoride release, Fourier-transformer infrared spectra, conductivity and swelling behavior are measured. It is found that chemical degradation causes predominant loss of side-chains. A transition from ductile to brittle fracture is observed with increasing degradation level. In addition, the cross-sections are examined to link fracture behavior with microstructure changes. While the decreased fracture toughness is attributed to reduced mechanical properties such as Young's modulus and break strain, the decreased crack propagation resistance is ascribed to reduced plastic zone size ahead of crack tip, which reduces the plastic energy dissipation. These findings not only provide new mechanical dataset of degraded membranes for performance and durability modelling to take into account of chemical degradation effect but also improve the understanding of membrane durability.
Fatigue life modeling for a low alloy steel after long-term thermal aging

Long Jin,Ming-Liang Zhu,Shang-Lin Zhang,Min Yang,Tian-Da Yu,Fu-Zhen Xuan

DOI: https://doi.org/10.1016/j.ijfatigue.2024.108645

IF: 5.489

2024-10-13

International Journal of Fatigue

Abstract:Fatigue failure of materials has a considerable impact on the safety of equipment in service. In this study, axially tensile and low cycle fatigue tests were conducted on a low alloy steel after accelerated thermal aged at 450 °C for 10,000 h. The experimental results indicate that the ultimate and yield strengths increase moderately, while the fatigue life of specimens experience a slight decrease in this circumstance. The fracture analysis demonstrates that the bainite breaking facilitates the fatigue crack initiation and propagation after thermal aging, which is accompanied by a decrease in plastic strain amplitude. Therefore, the plastic strain amplitude is considered as an indicator of thermal aging in fatigue life modeling for the low alloy steel. Finally, a novel life model that incorporates both aging time and temperature was proposed for rapid prediction of low cycle fatigue life. It is assumed that this model promotes reliable fatigue life prediction in low alloy steels under various thermal aging circumstances, as well as the extrapolation of fatigue performance of the material in service.

materials science, multidisciplinary,engineering, mechanical
Fracture and Fatigue of Thin Crystalline SrTiO$_3$ Membranes

Varun Harbola,Ruijuan Xu,Samuel Crossley,Prastuti Singh,Harold Y. Hwang

DOI: https://doi.org/10.1063/5.0060465

2021-07-27

Abstract:The increasing availability of a variety of two-dimensional materials has generated enormous growth in the field of nanoengineering and nanomechanics. Recent developments in thin film synthesis have enabled the fabrication of freestanding functional oxide membranes that can be readily incorporated in nanomechanical devices. While many oxides are extremely brittle in bulk, recent studies have shown that, in thin membrane form, they can be much more robust to fracture as compared to their bulk counterparts. Here, we investigate the ultimate tensile strength of SrTiO$_3$ membranes by probing freestanding SrTiO$_3$ drumheads using an atomic force microscope. We demonstrate that SrTiO$_3$ membranes can withstand an elastic deformation with an average strain of ~6% in the sub-20 nm thickness regime, which is more than an order of magnitude beyond the bulk limit. We also show that these membranes are highly resilient upon a high cycle fatigue test, surviving up to a billion cycles of force modulation at 85% of their fracture strain, demonstrating their high potential for use in nanomechanical applications.

Applied Physics,Materials Science
Characterization of biaxial fatigue durability for fuel cell membranes using pressure-loaded blisters

Qiang Lin,Yihao Yao,Gang Chen,Xu Chen,Shouwen Shi

DOI: https://doi.org/10.1016/j.polymertesting.2023.108127

IF: 5.1

2023-08-01

Polymer Testing

Abstract:In this study, a customized pressure-loaded blister test device capable of achieving sinusoidal control of pressure was developed to investigate the biaxial fatigue durability of proton exchange membrane (PEM) for fuel cells. The effect of temperature, relative humidity and stress state on biaxial fatigue life was investigated, and the biaxial stress-strain curves under different temperature and relative humidity conditions were also compared. It is found that increasing pressure induces higher biaxial stress and exacerbates the accumulation of plastic strain in the membrane, which adversely affects biaxial fatigue lifetime of PEM. Increasing temperature and decreasing humidity reduces the biaxial yield strength, thereby reducing the fatigue life of membrane. In addition, lowering temperature can lead to a transition in the failure mode from complete rupture to leakage failure. The increase in air pressure ratio, Rp, (minimum to maximum pressure ratio) also leads to premature membrane failure.

materials science, characterization & testing,polymer science
Structure–property Relationship Study of Nafion XL Membrane for High-Rate, Long-Lifespan, and All-Climate Vanadium Flow Batteries

Lihong Yu,Feng Lin,Ling Xu,Jingyu Xi

DOI: https://doi.org/10.1039/c7ra04996j

IF: 4.036

2017-01-01

RSC Advances

Abstract:The sandwich-structured Nafion XL membrane is promising for vanadium flow batteries to achieve high-rate performance, super-long lifespan and broad temperature adaptability.
Effect of catalyst layer on fatigue life and fracture mechanisms of fuel cell membrane

Shouwen Shi,Jiayao Li,Bingshuang Gao,Hailong Dai,Qiang Lin,Xu Chen

DOI: https://doi.org/10.1111/ffe.13626

2021-12-12

Abstract:Perfluorosulfonic acid (PFSA) membrane in polymer‐electrolyte fuel cells bears cyclic mechanical stress during humidity cycles under actual operation conditions, and its durability severely influences the life of fuel cells. However, the fatigue failure mechanisms of membranes are still not clear. In order to investigate the effect of catalyst layer on the fatigue life and fatigue fracture mechanisms of PFSA membranes, fatigue tests of Nafion 212 membranes and two catalyst‐coated membranes (CCMs) are conducted. The morphologies of membranes at different stages of fatigue crack initiation and propagation are identified. It is found that crack initiates from both surfaces of Nafion 212 membrane. Compared with Nafion 212 membrane, the fatigue life of single‐sided CCM increases by more than three times, while that of double‐sided CCM increases by 13 times. Such a phenomenon is ascribed to the protection of catalyst layer on membrane surface, which delays fatigue cracks initiation.

materials science, multidisciplinary,engineering, mechanical
Experimental investigation of the fatigue of closed-cell aluminum alloy foam

m d zhao,xueling fan,qinzhi fang,t j wang

DOI: https://doi.org/10.1016/j.matlet.2015.07.040

IF: 3

2015-01-01

Materials Letters

Abstract:Tension–tension fatigue tests are carried out to investigate the fatigue of closed-cell aluminum alloy foam. The stress–life (S–N) curve of the foam is obtained, in which large scatter is observed and discussed in detail. To understand the scatter of fatigue life of the foam, fracture surface is examined. The fatigue life decreases as the number and the size of large cells increase. The irregularity of inner cell structure of the foam attributes to the scatter of fatigue life. Then, a statistical stress–life model is developed, and a series of statistical probability–stress–life (P–S–N) curves are obtained. The P–S–N curve is efficient in describing the fatigue of foam materials.
Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

Wei Li,Rui Sun,Tianyi Hu,Xiaolong Li,Cheng Li,Yucheng Zhang,Xiaoming Ding,Ping Wang

DOI: https://doi.org/10.1016/j.ijfatigue.2021.106250

IF: 5.489

2021-07-01

International Journal of Fatigue

Abstract:Axial loading tests with stress ratios of -1 and 0.1 at 25°C and 650°C were performed to investigate the effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of a Ni-based superalloy manufactured by selective laser melting. Interior fatigue failure with longer life is greatly promoted at elevated temperature, which is induced from the crystallographic facets associated with grain structure. By means of electron-backscattered diffraction and stress intensity factor evaluation, the interior failure mechanisms are elucidated. Based on the proposed microstructure-based crack nucleation life model, a good agreement between the predicted and experimental results is obtained.

materials science, multidisciplinary,engineering, mechanical
Experimental Study and Numerical Simulation on High Temperature & Low Cycle Short Fatigue Cracks under Multiaxial Stress States

YU Miao,WANG Zheng,WANG Lei

DOI: https://doi.org/10.3969/j.issn.1001-4837.2006.11.001

2006-01-01

Abstract:Low cycle short fatigue cracks at high temperature was experimentally studied with the material 16MnR under multiaxial stress.A stochastic distribution evolution of collective short fatigue cracks model is established based on the experiment analysis results.The model refers to the effect of material microstructure and interference influence between cracks.The whole process of short fatigue cracks initiation,propagation,coalescence and interference on the surface of material 16MnR is numerically simulated by means of this model.The result is that the simulation results are basically consistent with the experiment results.The model can be used to simulate the short cracks effectively.The definitions of micro short crack initiation drive force and propagation drive force are established.
Effect of test temperature on low cycle fatigue behavior of zircaloy-4

Lin Xiao,HaiCheng Gu

1994-01-01

Abstract:Symmetric tension-compression LCF properties at RT and 400��C was studied for Zircaloy-4 after stress relief annealing treatment. The testing results include the relationships of stress-strain under cyclic and monotonic loading and the effects of test temperature on cyclic deformation behavior and fatigue properties. The fatigue life prediction method for zircaloy at high temperature was also discussed. All these results were rationalized in terms of fatigue fracture modes based on the SEM examination of fracture surfaces. The results show that cyclic stress-strain curves of zircaloy-4 behave as cyclic hardening behavior at room temperature and cyclic softening behavior at 400��C respectively.
Modeling of Fatigue for Cellular Materials

Huang J. S.,Lin J. Y.

DOI: https://doi.org/10.1557/proc-521-27

1998-01-01

Abstract:Dimensional arguments are used to analyze the fatigue of cellular materials. A modeling describing the fatigue of foams with or without macrocrack is derived and compared to the existing experimental data of cementitious foams and phenolic foams; agreement is good.

Fatigue response of Nafion® XL membrane in biaxial tension: Temperature effects

Temperature-dependent fatigue crack growth mechanisms of fuel cell membranes

Effects of Microstructure on the Retention of Proton Conductivity of Nafion/SiO2 Composite Membranes at Elevated Temperatures:An in Situ SAXS Study

Temperature‐dependent mechanical performance of Nafion® 212 proton exchange membrane under uniaxial and biaxial loading

Continuum Approach for Modeling Mechanical Fatigue of Ionomer Membrane

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Fatigue crack propagation behavior of fuel cell membranes after chemical degradation

Impact of Initial Cyclic Loading on Mechanical Properties and Performance of Nafion

Effect of temperature on dynamic fatigue behaviour of Si3N4 material

Research on the Fatigue Properties of Glass Fiber Composite Laminates

Embrittlement Induced Fracture Behavior and Mechanisms of Perfluorosulfonic-Acid Membranes after Chemical Degradation

Fatigue life modeling for a low alloy steel after long-term thermal aging

Fracture and Fatigue of Thin Crystalline SrTiO$_3$ Membranes

Characterization of biaxial fatigue durability for fuel cell membranes using pressure-loaded blisters

Structure–property Relationship Study of Nafion XL Membrane for High-Rate, Long-Lifespan, and All-Climate Vanadium Flow Batteries

Effect of catalyst layer on fatigue life and fracture mechanisms of fuel cell membrane

Experimental investigation of the fatigue of closed-cell aluminum alloy foam

Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

Experimental Study and Numerical Simulation on High Temperature & Low Cycle Short Fatigue Cracks under Multiaxial Stress States

Effect of test temperature on low cycle fatigue behavior of zircaloy-4

Modeling of Fatigue for Cellular Materials