Preparation of Absorption Sphere of High Temperature Gas Cooled Reactor

T Guo,C Wang,LM Doug,J Liu,B Zhu,TX Liang
2013-01-01
Rare Metal Materials and Engineering
Abstract:With B4C and graphite as the filler, and Phenolic resin 217 as the binder, block samples of 10 mmx10 mmx10 mm and absorption sphere samples of diameter Phi(6 +/- 0.25) mm were prepared. Shimadzu AG-IC20KN electronic universal testing machine was used to test the crushing force of the samples. The relationship between the structure and properties of the block samples were studied. The results show that pretreating B4C with resin is conducive to bonding. The impregnation could improve the compressive strength. With increasing the impregnation times, the compressive strength is increased. The compressive strength is greater when the thermosetting resin is used as impregnant. The average value of crushing force of absorption sphere obtained by the optimal process is up to 600 N.