Abstract:Titania nanowire arrays have been deposited on Ti foils through direct oxidizing the Ti substrate with aqueous hydrogen peroxide solutions containing melamine and nitric acid, and the applicability of such nanowire arrays to back-illuminated dye-sensitized solar cells studied in parallel with titania nanotube arrays on Ti foils. The low-temperature nitrogen adsorption measurement reveals that the film with nanowires 25nm in diameter and 1μm in length possesses a BET specific surface area of 59.0m2g−1, a value much larger than 26m2g−1 calculated for the nanotube with an inner diameter of 80nm, an outer diameter of 120nm and a total length of 3μm. Assuming an indirect transition between band gaps, the nanowire film exhibits a bandgap of 3.1eV, slightly larger than that of 3.0eV for the nanotube one. A detailed electrochemical study suggests that, in comparison with the nanotube film, the nanowire one exhibits much lower saturated photocurrent and poorer conductivity under the Xe-lamp irradiation. However, when utilized to construct back-side illuminated dye-sensitized solar cells, the cell with the 2μm-thick nanowire photoanode possesses significantly higher efficiency than the one with the 3μm-thick nanotube photoanode. The relatively high energy conversion efficiency is contributed to the high specific surface area and the unique mesoporous structure of the titania nanowire arrays, which favors the adsorption of dye molecules.

Fabrication of MgO Coated TiO2 Nanowires Films and Application in Dye Sensitized Solar Cells

Fabrication of MgO-Coated TiO_2 Nanowires Films and Application in Dye-Sensitized Solar Cells

Electron Transport in Dye-Sensitized Solar Cells Based on TiO 2 Nanowires

Fabrication of Highly-Oriented TiO2 Nanotube Arrays and Its Application in Dye-Sensitized Solar Cells

The Preparation of TiO2 Nanotube by ZnO Nanorod Template Method and Application in Dye-Sensitized Solar Cells

Fabrication and Photoelectrochemical Performance of CdS Quantum Dots Sensitized TiO2 Film Electrodes

A novel approach to titania nanowire arrays as photoanodes of back-illuminated dye-sensitized solar cells

ZnO/TiO2 Composite Photoanodes for Efficient Dye-Sensitized Solar Cells

Open-circuit voltage improvement by using TiO2 nanotubes as a working electrode of dye-sensitized solar cell

Hybrid TiO2–SnO2 Nanotube Arrays for Dye-Sensitized Solar Cells

Ordered TiO2 Nanotube Arrays on Transparent Conductive Oxide for Dye-Sensitized Solar Cells

High-Efficiency Solid-State Dye-Sensitized Solar Cells Based on Tio2-Coated Zno Nanowire Arrays

ZnO/TiO 2 Core–shell Nanowire Arrays for Enhanced Dye-Sensitized Solar Cell Efficiency

Improved photovoltaic performance of dye-sensitized solar cells (DSSCs) by Zn + Mg co-doped TiO2 electrode

Fabrication of Morphology Controllable Rutile TiO2 Nanowire Arrays by Solvothermal Route for Dye-Sensitized Solar Cells

COATING EFFECT OF TiO2 PHOTOANODE FOR DYE-SENSITIZED SOLAR CELL

Growth of ZnO/TiO2 Nanostructured Composite Films and Its Application in Dye-Sensitized Solar Cells

Application of TiO2 nanoparticles coated multi-wall carbon nanotube to dye-sensitized solar cells

Low-Cost Fabrication of TiO2 Nanorod Photoelectrode for Dye-sensitized Solar Cell Application

TiO2 coated SnO2 nanosheet films for dye-sensitized solar cells

TiO2 nanotube based dye-sensitized photoanode