Abstract:In the modern competitive world environment, the foundry industry must efficiently perform with very few rejections. The casting process is completed in three steps: pre-casting, casting, and post-casting. The primary casting Process involves charging the furnace, melting metal, holding it at certain temperatures, and pouring operation. The post-casting includes inspection and dispatch. The industry focuses on lower manufacturing costs with high productivity. Manufacturing high-quality products in less time without any defects is a goal of every foundry industry. Various casting defects such as shrinkage, porosity, surface finish, cold shut, and extra material are common. There is a direct impact of these defects on an organization’s quality, productivity, and profitability. Castings without any defect and minimum cost of production are desired for the foundries. In the present case study, data is collected from the foundry. The study of various causes of defects and product rejection during the High-Pressure Die Casting (HPDC) is conducted. Cylinder block castings was selected for analysis which are made up of aluminum alloy used in engines of automobiles. Defects in casting are the limitations of the casting process. This study provides knowledge of casting defects and their root cause analysis. This paper uses the Pareto analysis technique to identify the primary defects. The critical areas are identified through the case study and prioritization of casting defects. The casting defects observed are arranged in decreasing order and discovered that 80% of rejections are due to casting defects like cold shut, shrinkage, soldering, stain, crack, and warpage. Further, a cause-and-effect analysis is conducted. The reasons have the most significant effects and suggestions are claimed for improved casting quality in the future.

Analysis of Cavity Defects of Die Castings by Fractal Theory and Statistic Method

Die Structure Optimization of Aluminum Alloy Wheel Low-Pressure Die Casting Based on CAE

Determination of casting parameters of thick wall die-casting of magnesium alloy and simulation of its processing

Quantitative Analysis of Pores for Die Casting Magnesium Alloys Based on Matlab

Investigation on Surface Defects Produced in Pretreatment of Die-casting AM60B Magnesium Alloy

The molding analysis of automobile parts using the die-casting system

Relationship Between Porosity Distribution and Mechanical Properties of Vacuum Die Casting AM50 Magnesium Alloy

Analysis of Formation Mechanism of Typical Defects in Aluminum (Magnesium) Alloys Castings by the Expendable Pattern Shell Casting with Vacuum and Low Pressure

Criteria for Prediction of Shrinkage Cavities and Porosity in Castings

Fracture Behavior of a High Pressure Die Casting AlSi10MnMg Alloy with Varied Porosity Levels

Studies on formation of shrinkage cavity and porosity of steel castings by taking filling process into account

Casting defects and microstructure distribution characteristics of aluminum alloy cylinder head with complex structure

Defect Analysis and Quality Control on Stainless Steel Investment Casting

Study on a CAD/CAE system of die casting

Identifying Critical Defect Sizes From Pore Clusters in Nickel-based Superalloys Using Automated Analysis and Casting Simulation

Stress and Distortion Simulation of Magnesium Alloy Die Casting Dies

Ductility prediction of HPDC aluminum alloy using a probabilistic ductile fracture model

Characterization on the formation of porosity and tensile properties prediction in die casting Mg alloys

Evaluation of Distortion of Castings

Analyzing casting defects in high-pressure die casting industrial case study

Study on scatter in mechanical properties of cylinder head with complex structure characters