In-situ synthesis of aluminum matrix nanocomposites by selective laser melting of carbon nanotubes modified Al-Mg-Sc-Zr alloys
Lixia Xi,Kai Ding,Han Zhang,Dongdong Gu
DOI: https://doi.org/10.1016/j.jallcom.2021.162047
IF: 6.2
2022-01-01
Journal of Alloys and Compounds
Abstract:<p>Aluminum matrix nanocomposites were manufactured by selective laser melting (SLM) of 0.5 wt% multi-walled carbon nanotubes (MWCNTs) modified Al-Mg-Sc-Zr alloys. The influence of MWCNT addition on the manufacturing quality, the phase formation and the mechanical properties of the Al-Mg-Sc-Zr alloys was investigated. It is found that primary Al<sub>3</sub>(Sc,Zr) particles precipitated and were uniformly dispersed in both equiaxed and columnar regions of the SLM-fabricated MWCNTs/Al-Mg-Sc-Zr nanocomposites. New Al<sub>4</sub>C<sub>3</sub> phase was generated either on the open tip or in the defected and amorphous carbon layer of the MWCNTs, covering their overall surface. The unreacted MWCNTs completely transferred to Al<sub>4</sub>C<sub>3</sub> upon heat treatment, forming a stable {003} Al<sub>4</sub>C<sub>3</sub>/{200}Al interface. The heat-treated MWCNTs/Al-Mg-Sc-Zr nanocomposites exhibit high microhardness of 169.0 ± 0.7 HV<sub>0.2</sub>, tensile strength of 544.2 ± 6.8 MPa, yield strength of 505.1 ± 6.3 MPa and elastic modulus of 97.8 ± 0.7 GPa, increasing by 6.3%, 4.5%, 5.0% and 5.6%, respectively, compared with the unmodified Al-Mg-Sc-Zr alloys. The improved performance was ascribed to the collective effects of precipitation strengthening of secondary Al<sub>3</sub>(Sc,Zr) nanoparticles, in-situ synthesis of Al<sub>4</sub>C<sub>3</sub> as well as favorable interfacial bonding for effective load transfer. This study can provide reference values for laser additive manufacturing of MWCNTs modified other metallic alloys to enhance their comprehensive properties.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering