Effect of Trace Element B on the Microstructure and Mechanical Properties of 8Cr4Mo4V Bearing Steel
Xingfu Yu,Ze Wu,Tianci Hao,Yong Su,Ying Jia,Yinghua Wei
DOI: https://doi.org/10.1002/srin.202400501
IF: 2.1258
2024-09-11
steel research international
Abstract:Adding 0.005% of B element to 8Cr4Mo4V bearing steel can increase the bainite content significantly, increase the precipitated carbide content by 23%, and decrease the residual austenite by 33%. In addition, the hardness of steel is increased by 12 Vickers hardness, the wear quality is reduced by 6%, and the wear resistance is improved. By means of salt‐bath austempering treatment, microstructure observation, X‐Ray diffraction analysis, microhardness measurement, and friction and wear performance tests for 8Cr4Mo4V steels with standard composition and with trace addition of 0.005% boron, the effect of boron on the phase composition and mechanical properties of the steel is studied. The results show that trace element boron greatly increases the content of needle‐like lower bainite in the quenched microstructure, promotes the dissolution of undissolved carbides, reduces the content of M/A island, but coarsens grains. After tempering, trace element B increases the amount of bainite generation, refines the lath martensite, and significantly promotes the precipitation of carbides, whose size is finer, and the distribution is more dispersed. In terms of mechanical properties, trace element B improves the hardness by promoting the precipitation of the second phase and refining the lath martensite, and the increase in the bainite content changes the wear mechanism and enhances the wear resistance.
metallurgy & metallurgical engineering